High Performance Bricks from Straw and Asphalt

Received: 28 November 2018     Accepted: 21 December 2018     Published: 22 January 2019
Views:       Downloads:
Abstract

This study investigated a partial replacement of clay by additives for bricks. The purified clay mixed with different volume percentage of additives (Asphalt and Straw from agricultural waste) as separate and both to cast as bricks with the standard dimensions of 18.5 × 8.5 × 6.5 cm3. Cylindrical pellets casted with the dimensions of average diameter of 40 mm and thicknesses about 2.5 ± 0.2mm. The casted bricks and pellets are air dried in open atmosphere for 8-10 days. These bricks and pellets are fired for three days, at the end of three days kiln is allowed to cool to reach room temperature. The sample bricks are tested for compressive strength and water absorption; pellets are tested for thermal conductivity and electrical conductivity. From the obtained results, it has concluded that the compressive strength slightly increased against density of the bricks. A moderate decrement observed in the water absorption against density of the samples and compressive strength weakens with the increment of water absorption of the samples. Improved electrical conductivities of the samples with additives appears change in electrical properties from insulating to semiconducting. Thermal conductivity values of the samples with additives are climb against the 100% clay sample. The result shows that the greatest thermal conductivity of 0.905 Wm-1K was obtained for 85% Clay / 5% Straw / 10% Asphalt sample. The additives enhance porosity and heat contact through the samples. The values obtained and with reference to the graphs plotted, can be concluded that the 90% Clay / 5% Straw / 5% Asphalt sample is superior among the samples.

Published in Composite Materials (Volume 2, Issue 1)
DOI 10.11648/j.cm.20180201.14
Page(s) 26-31
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2019. Published by Science Publishing Group

Keywords

Clay, Asphalt, Straw, Compressive Strength, Water Absorption, Electrical Conductivity, Thermal Conductivity

References
[1] Ateater HA, Ellickson T. Remanent Magnetization of Ancient Bricks. Nature. 1958, 181: 404.
[2] GokhanG, Osman S. Porous Clay Bricks Manufactured With Rice Husks. Construction and Building Materials. 2013, 40: 390–396.
[3] Sutas J, Mana A, Pitak L. Effect of Rice Husk and Rice Husk Ash to Properties of Bricks. Procedia Engineering.2012, 32: 1061 – 1067.
[4] WatileRK, Deshmukh SK, DurgePV, Yawale AD. Utilization of Rice Husk For Production of Clay Brick. International Journal of Research in Advent Technology. 2015: 199-203.
[5] Ashish KumarP, Rinku P. Comparative Study of Compressive Strength of Bricks Made With Various Materials to Clay Bricks. International Journal of Scientific and Research Publications. 2012, 2(7): 1-4.
[6] Sitpalan A, Ananda EMS, Aashik AR, Preththiha V, Rajitha VKM and Suventhiran S. Feasibility of Natural Clay Additives in Cement Mortar. RRJPAP, 2018, 6(1): 01-07.
[7] ASTM C109 Standard Test Method for Compressive Strength of Hydraulic Cement Mortars. https://www.astm.org/Standards/C109. 15th October 2018.
[8] Kim KH, Jeon SE, Kim JK, Yang S. An experimental study on thermal conductivity of concrete. Cement and concrete research, 2003;33 (3):363-371.
[9] Adekunle A, et al. Analysis of Thermal and Electrical Properties of Laterite, Clay and Sand Samples and Their Effects on Inhabited Buildings in Ota, Ogun State, Nigeria. Journal of Sustainable Development Studies. 2014;6:391-412.
[10] Leonel RF, et al. Characterization of soil-cement bricks with incorporation of used foundry sand. Cerâmica. 2017;63:329-335.
[11] Badr El-Din EH, Hanan AF, Ahmed MH. Incorporation of water sludge, silica fume, and rice husk ash in brick making. Advances in Environmental Research. 2012; 1(1): 83-96.
[12] Cultrone G, De La Torre MJ, Sebastian EM, Cazalla O, Rodriguez-Navarro C. Behavior of brick samples in aggressive environments. Water Air and Soil Pollution. 2000; 119:191–207.
[13] Cultrone, G, Sebastián E, Elert K, De La Torre MJ, Cazalla O, Rodriguez-Navarro C. Influence of mineralogy and firing temperature on the porosity of bricks. Journal of the European Ceramic Society. 2004; 24:547–564.
[14] Bahobail MA. The mud additives and their effect on thermal conductivity of adobe bricks. Journal of Engineering Sciences, Assiut University, 2012; 40 (1): 21-34.
Cite This Article
  • APA Style

    Sitpalan Ahilan, Dharani Sandunika Abeysinghe, Kolitha Fernando, Thilini Priyadarshi Herath. (2019). High Performance Bricks from Straw and Asphalt. Composite Materials, 2(1), 26-31. https://doi.org/10.11648/j.cm.20180201.14

    Copy | Download

    ACS Style

    Sitpalan Ahilan; Dharani Sandunika Abeysinghe; Kolitha Fernando; Thilini Priyadarshi Herath. High Performance Bricks from Straw and Asphalt. Compos. Mater. 2019, 2(1), 26-31. doi: 10.11648/j.cm.20180201.14

    Copy | Download

    AMA Style

    Sitpalan Ahilan, Dharani Sandunika Abeysinghe, Kolitha Fernando, Thilini Priyadarshi Herath. High Performance Bricks from Straw and Asphalt. Compos Mater. 2019;2(1):26-31. doi: 10.11648/j.cm.20180201.14

    Copy | Download

  • @article{10.11648/j.cm.20180201.14,
      author = {Sitpalan Ahilan and Dharani Sandunika Abeysinghe and Kolitha Fernando and Thilini Priyadarshi Herath},
      title = {High Performance Bricks from Straw and Asphalt},
      journal = {Composite Materials},
      volume = {2},
      number = {1},
      pages = {26-31},
      doi = {10.11648/j.cm.20180201.14},
      url = {https://doi.org/10.11648/j.cm.20180201.14},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.cm.20180201.14},
      abstract = {This study investigated a partial replacement of clay by additives for bricks. The purified clay mixed with different volume percentage of additives (Asphalt and Straw from agricultural waste) as separate and both to cast as bricks with the standard dimensions of 18.5 × 8.5 × 6.5 cm3. Cylindrical pellets casted with the dimensions of average diameter of 40 mm and thicknesses about 2.5 ± 0.2mm. The casted bricks and pellets are air dried in open atmosphere for 8-10 days. These bricks and pellets are fired for three days, at the end of three days kiln is allowed to cool to reach room temperature. The sample bricks are tested for compressive strength and water absorption; pellets are tested for thermal conductivity and electrical conductivity. From the obtained results, it has concluded that the compressive strength slightly increased against density of the bricks. A moderate decrement observed in the water absorption against density of the samples and compressive strength weakens with the increment of water absorption of the samples. Improved electrical conductivities of the samples with additives appears change in electrical properties from insulating to semiconducting. Thermal conductivity values of the samples with additives are climb against the 100% clay sample. The result shows that the greatest thermal conductivity of 0.905 Wm-1K was obtained for 85% Clay / 5% Straw / 10% Asphalt sample. The additives enhance porosity and heat contact through the samples. The values obtained and with reference to the graphs plotted, can be concluded that the 90% Clay / 5% Straw / 5% Asphalt sample is superior among the samples.},
     year = {2019}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - High Performance Bricks from Straw and Asphalt
    AU  - Sitpalan Ahilan
    AU  - Dharani Sandunika Abeysinghe
    AU  - Kolitha Fernando
    AU  - Thilini Priyadarshi Herath
    Y1  - 2019/01/22
    PY  - 2019
    N1  - https://doi.org/10.11648/j.cm.20180201.14
    DO  - 10.11648/j.cm.20180201.14
    T2  - Composite Materials
    JF  - Composite Materials
    JO  - Composite Materials
    SP  - 26
    EP  - 31
    PB  - Science Publishing Group
    SN  - 2994-7103
    UR  - https://doi.org/10.11648/j.cm.20180201.14
    AB  - This study investigated a partial replacement of clay by additives for bricks. The purified clay mixed with different volume percentage of additives (Asphalt and Straw from agricultural waste) as separate and both to cast as bricks with the standard dimensions of 18.5 × 8.5 × 6.5 cm3. Cylindrical pellets casted with the dimensions of average diameter of 40 mm and thicknesses about 2.5 ± 0.2mm. The casted bricks and pellets are air dried in open atmosphere for 8-10 days. These bricks and pellets are fired for three days, at the end of three days kiln is allowed to cool to reach room temperature. The sample bricks are tested for compressive strength and water absorption; pellets are tested for thermal conductivity and electrical conductivity. From the obtained results, it has concluded that the compressive strength slightly increased against density of the bricks. A moderate decrement observed in the water absorption against density of the samples and compressive strength weakens with the increment of water absorption of the samples. Improved electrical conductivities of the samples with additives appears change in electrical properties from insulating to semiconducting. Thermal conductivity values of the samples with additives are climb against the 100% clay sample. The result shows that the greatest thermal conductivity of 0.905 Wm-1K was obtained for 85% Clay / 5% Straw / 10% Asphalt sample. The additives enhance porosity and heat contact through the samples. The values obtained and with reference to the graphs plotted, can be concluded that the 90% Clay / 5% Straw / 5% Asphalt sample is superior among the samples.
    VL  - 2
    IS  - 1
    ER  - 

    Copy | Download

Author Information
  • Department of Physics, Faculty of Science, Eastern University Sri Lanka, Vantharumoolai, Sri Lanka

  • Department of Physics, Faculty of Science, Eastern University Sri Lanka, Vantharumoolai, Sri Lanka

  • Department of Physics, Faculty of Science, Eastern University Sri Lanka, Vantharumoolai, Sri Lanka

  • Department of Physics, Faculty of Science, Eastern University Sri Lanka, Vantharumoolai, Sri Lanka

  • Sections