Mixed Agro-waste Biocomposites of Low Density Polyethene; Impact of Fillers on Mechanical, Morphological, Water Imbibition and Biodegradability Properties

Received: 1 August 2021     Accepted: 12 August 2021     Published: 23 August 2021
Views:       Downloads:
Abstract

In retrospect, the incorporation of agricultural waste as a natural, biodegradable filler in polymer composites is a scientific innovation that has received global attention. This is due to its impact in enhancing sustainability of composites and degradation of plastics. The mechanical, morphological, water imbibition and biodegradability properties of low density polyethene produced composites were investigated using agro wastes blend of corn cobs and sugarcane bagasse. Agro waste with a particle size of 75μm was blended in a 50:50 ratio and integrated into LDPE polymer matrix at different percentages of 0%, 5%, 10%, 15%, and 20%, with composites fabricated via injection molding. The mechanical properties like the tensile strength, percentage elongation at break, compressive strength, shear modulus and hardness test of the composites were studied in line with ASTM standards. Also, the morphological properties were studied with a Scanning Electron Microscope. From the results, there was a reduction in tensile strength of the composites with increasing filler loading. However, the percentage elongation at break of the LDPE composite increased as the filler loading increased as an indication that the composite is relatively ductile. Hardness, compressive strength and shear modulus of the polymer composites increased with increasing filler loading. Morphological study of the composites showed a good adhesion and interfacial bonding between the filler and the polymer matrix due to good dispersion of the fillers in the polymer matrix. Biodegradation test revealed a reduction in the mass of the composites after a 3- month burial period which was more pronounced after a 30-day test period indicating that the composite is more environmentally friendly. The highest degradation rate was observed at 20wt% CCSB-LDPE composite giving a 15% reduction after 90days. Result from the water imbibition test indicated no increase in the mass of the composites after immersion in water. This is an indication that the composite can be utilized in wet environments. Hence, from the findings, it is suggested that agro-wastes like rice husk and sugarcane bagasse be employed as fillers in the manufacture of plastics because they are cheaper and viable. Finally, the produced plastics would degrade when discarded.

Published in American Journal of Polymer Science and Technology (Volume 7, Issue 3)
DOI 10.11648/j.ajpst.20210703.12
Page(s) 44-49
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2021. Published by Science Publishing Group

Keywords

Agro-waste, Low Density Polyethene, Mechanical and Morphological Properties, Water Absorption, Biodegradation

References
[1] Ofora, P. U., Nwokoye, J. N., Ekpunobi, E. U., Okpalaunegbu, C. A., Ezeanyika, M., (2016). Effects of Bamboo-Corn Husk as Fillers on the Mechanical Properties in Polypropylene. International Journal of Materials Chemistry and Physics, 2 (2): 88-92.
[2] Chitra, J. N., and Vasanthakumari, R., (2012). Studies on polypropylene biocomposite with cornhusk waste. International Journal of Scientific and Engineering Research, 3 (7): 562-564.
[3] Vidyashri, V., Lewis, H., Narayanasamy, P., Mahesha, G. T., Bhat, K. S., (2019). Preparation of chemically treated sugarcane bagasse fiber reinforced epoxy composites and their characterization. Cogent Engineering, 6 (1): 1-20.
[4] Agunsoye, J. O., and Aigbodion, V. S. (2013)., Bagasse filled recycled polyethene bio-composites: Morphological and mechanical properties study. Results in Physics, 3: 187-194.
[5] Thakur, V. K., and Kessler, M. R., (2014). Free radical induced graft copolymerization of ethyl acrylate onto soy for multifunctional materials. Materials Today Communications, 1 (1-2): 34-41.
[6] Chen, R. S., Ab Ghani, M. H., Ahmad, S., Salleh, M. N., Tarawneh, M. A. A., (2015). Rice husk flour biocomposites based on recycled high-density polyethene/polyethene terephthalate blend: Effect of high filler loading on physical, mechanical and thermal properties. Journal of Composite Materials, 49 (10): 1241-1253.
[7] Kumar, S., Mer, K. K. S., Gangil, B., Patel, V. K., (2019). Synergy of rice-husk filler on physico-mechanical and tribological properties of hybrid Bauhinia-vahlii/sisal fiber reinforced epoxy composites. Journal of Materials Research and Technology, 8 (2): 2070-2082.
[8] Mishra, A., (2017). Mechanical properties of cocconut shell dust, epoxy-fly ash hybrid composites. American Journal of Engineering Research, 6 (9): 166-174.
[9] Bekele, L. D., Zhang, W., Liu, Y., Duns, G. J., Yu, C., Jin, L., Li, X., Chen, J., (2017). Impact of cotton stalk biomass weathering on the mechanical and thermal properties of cotton stalk flour/linear low density polyethene (LLDPE) composites. Journal of Biobased Materials and Bioenergy, 11 (1): 27-33.
[10] Nguyen, H., Moghadam, M. J., Moayedi, H., (2019). Agricultural wastes preparation, management, and applications in civil engineering: a review. Journal of Material Cycles and Waste Management, 21: 1039-1051.
[11] Prithivirajan, R., Jayabal, S., Bharathiraja, G., (2015). Bio-based composites from waste agricultural residues: Mechanical and morphological properties. Cellulose Chemistry and Technology, 49 (1): 65-68.
[12] Salmah, H., Ismail, A., Bakar A., (2005). Dynamic vulcanization of paper sludge filled polypropylene (PP)/ethylene propylene dienetherpolymer (EPDM). Malaysian Journal of Microscopy, 2: 15–22.
[13] Chris-Okafor P. U, Arinze R. U, Ekpunobi U. E, Anugwom M. C., (2018). Effects of mixed rice husk and corn cob as fillers on some properties of flexible polyether foam. Global Journal of Science Frontier Research, 17 (2): 30-37.
[14] Zhang, Q., Weiming, Y., Zhihe, Li., Lihong, W., and Hongzhen C., (2018). Mechanical Properties of Rice Husk Biochar Reinforced High Density Polyethene Composites, Polymers, 10: 286-296.
[15] Maya Jacob; Sabu Thomas; K. T. Varughese (2004). Mechanical properties of sisal/oil palm hybrid fiber reinforced natural rubber composites. Composites Science and Technology 64 (7-8): 955–965.
[16] Cautinho, f. M. B., Caota, T. H. S. and Carvalho, d. L. (1997). Polypropylene-wood fiber composites: Effect of treatment and mixing condition on mechanical properties. Composites, 43: 154–159.
[17] Morreale, M., Scaffaro, R., Maio, A. & La Mantia, F. P. (2007). Effect of adding wood flour to the physical properties of a biodegradable polymer. Composite, 42: 214-225.
[18] Abdullah, A., Rusel, D., and Abdulwahab, A., (2011). Water absorption and mechanical properties of high – density polyethene/ egg shell composite. Journal of Basrah Researches (Sciences), 37 (15): 1-8.
[19] Kricheldorf, H., Nuyken, O., and Swift, G., (2005). Hand book of Polymer Synthesis, Second Edition, Marcel Dekker.
[20] Chris-Okafor, P., Okonkwo, C., Ohaeke, M., (2018). Reinforcement of High Density Polyethene with Snail Shell Powder, American Journal of Polymer Science, 8 (1): 17-21.
[21] Onuegbu T. U., (2012); Study on the Effect of Coconut and Palm Kernel Shells on Density, Porosity Index and Tensile Properties of Flexible Polyether Foam. ARPN Journal of Science and Technology 2 (6).
[22] Kuan, C. f., Kuan, H. C., Ma, C. C. M. & Haung, c. M. (2006). Mechanical, thermal and morphological properties of water-crosslinked wood flour reinforced linear low-density polyethene composites, Composites, Part A, 37: 1696–1707.
[23] Amir, N., Ashori, A., Kazemi T., Ali, (2014). Characterization and biodegradability of polypropylene composites using agricultural residues and waste fish. Composites Part B: Engineering, 56 (2014): 279–283.
[24] Oldak, D., Kaczmarek, H., Buffeteau, T., Sourisseau, C., (2006). Photo and bio-degradation processes in polyethene, cellulose and their blends studied by ATR-FTIR and Raman spectroscopies. Journal of Material Science; 40 (16): 4189–4198.
[25] Nwanonenyi, S. C., Obidiegwu, M. U., Onuegbu, G. C., (2013). Effects of Particle Sizes, Filler Contents and Compatibilization on the Properties of Linear Low Density Polyethene Filled Periwinkle Shell Powder. The International Journal of Engineering and Science (IJES), 2 (2): 1-8.
Cite This Article
  • APA Style

    Marcellinus Chibuike Ogudo, Pauline Uchechukwu Chris-Okafor, Joy Nwando Nwokoye, Juliana Ozioma Anekwe. (2021). Mixed Agro-waste Biocomposites of Low Density Polyethene; Impact of Fillers on Mechanical, Morphological, Water Imbibition and Biodegradability Properties. American Journal of Polymer Science and Technology, 7(3), 44-49. https://doi.org/10.11648/j.ajpst.20210703.12

    Copy | Download

    ACS Style

    Marcellinus Chibuike Ogudo; Pauline Uchechukwu Chris-Okafor; Joy Nwando Nwokoye; Juliana Ozioma Anekwe. Mixed Agro-waste Biocomposites of Low Density Polyethene; Impact of Fillers on Mechanical, Morphological, Water Imbibition and Biodegradability Properties. Am. J. Polym. Sci. Technol. 2021, 7(3), 44-49. doi: 10.11648/j.ajpst.20210703.12

    Copy | Download

    AMA Style

    Marcellinus Chibuike Ogudo, Pauline Uchechukwu Chris-Okafor, Joy Nwando Nwokoye, Juliana Ozioma Anekwe. Mixed Agro-waste Biocomposites of Low Density Polyethene; Impact of Fillers on Mechanical, Morphological, Water Imbibition and Biodegradability Properties. Am J Polym Sci Technol. 2021;7(3):44-49. doi: 10.11648/j.ajpst.20210703.12

    Copy | Download

  • @article{10.11648/j.ajpst.20210703.12,
      author = {Marcellinus Chibuike Ogudo and Pauline Uchechukwu Chris-Okafor and Joy Nwando Nwokoye and Juliana Ozioma Anekwe},
      title = {Mixed Agro-waste Biocomposites of Low Density Polyethene; Impact of Fillers on Mechanical, Morphological, Water Imbibition and Biodegradability Properties},
      journal = {American Journal of Polymer Science and Technology},
      volume = {7},
      number = {3},
      pages = {44-49},
      doi = {10.11648/j.ajpst.20210703.12},
      url = {https://doi.org/10.11648/j.ajpst.20210703.12},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ajpst.20210703.12},
      abstract = {In retrospect, the incorporation of agricultural waste as a natural, biodegradable filler in polymer composites is a scientific innovation that has received global attention. This is due to its impact in enhancing sustainability of composites and degradation of plastics. The mechanical, morphological, water imbibition and biodegradability properties of low density polyethene produced composites were investigated using agro wastes blend of corn cobs and sugarcane bagasse. Agro waste with a particle size of 75μm was blended in a 50:50 ratio and integrated into LDPE polymer matrix at different percentages of 0%, 5%, 10%, 15%, and 20%, with composites fabricated via injection molding. The mechanical properties like the tensile strength, percentage elongation at break, compressive strength, shear modulus and hardness test of the composites were studied in line with ASTM standards. Also, the morphological properties were studied with a Scanning Electron Microscope. From the results, there was a reduction in tensile strength of the composites with increasing filler loading. However, the percentage elongation at break of the LDPE composite increased as the filler loading increased as an indication that the composite is relatively ductile. Hardness, compressive strength and shear modulus of the polymer composites increased with increasing filler loading. Morphological study of the composites showed a good adhesion and interfacial bonding between the filler and the polymer matrix due to good dispersion of the fillers in the polymer matrix. Biodegradation test revealed a reduction in the mass of the composites after a 3- month burial period which was more pronounced after a 30-day test period indicating that the composite is more environmentally friendly. The highest degradation rate was observed at 20wt% CCSB-LDPE composite giving a 15% reduction after 90days. Result from the water imbibition test indicated no increase in the mass of the composites after immersion in water. This is an indication that the composite can be utilized in wet environments. Hence, from the findings, it is suggested that agro-wastes like rice husk and sugarcane bagasse be employed as fillers in the manufacture of plastics because they are cheaper and viable. Finally, the produced plastics would degrade when discarded.},
     year = {2021}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Mixed Agro-waste Biocomposites of Low Density Polyethene; Impact of Fillers on Mechanical, Morphological, Water Imbibition and Biodegradability Properties
    AU  - Marcellinus Chibuike Ogudo
    AU  - Pauline Uchechukwu Chris-Okafor
    AU  - Joy Nwando Nwokoye
    AU  - Juliana Ozioma Anekwe
    Y1  - 2021/08/23
    PY  - 2021
    N1  - https://doi.org/10.11648/j.ajpst.20210703.12
    DO  - 10.11648/j.ajpst.20210703.12
    T2  - American Journal of Polymer Science and Technology
    JF  - American Journal of Polymer Science and Technology
    JO  - American Journal of Polymer Science and Technology
    SP  - 44
    EP  - 49
    PB  - Science Publishing Group
    SN  - 2575-5986
    UR  - https://doi.org/10.11648/j.ajpst.20210703.12
    AB  - In retrospect, the incorporation of agricultural waste as a natural, biodegradable filler in polymer composites is a scientific innovation that has received global attention. This is due to its impact in enhancing sustainability of composites and degradation of plastics. The mechanical, morphological, water imbibition and biodegradability properties of low density polyethene produced composites were investigated using agro wastes blend of corn cobs and sugarcane bagasse. Agro waste with a particle size of 75μm was blended in a 50:50 ratio and integrated into LDPE polymer matrix at different percentages of 0%, 5%, 10%, 15%, and 20%, with composites fabricated via injection molding. The mechanical properties like the tensile strength, percentage elongation at break, compressive strength, shear modulus and hardness test of the composites were studied in line with ASTM standards. Also, the morphological properties were studied with a Scanning Electron Microscope. From the results, there was a reduction in tensile strength of the composites with increasing filler loading. However, the percentage elongation at break of the LDPE composite increased as the filler loading increased as an indication that the composite is relatively ductile. Hardness, compressive strength and shear modulus of the polymer composites increased with increasing filler loading. Morphological study of the composites showed a good adhesion and interfacial bonding between the filler and the polymer matrix due to good dispersion of the fillers in the polymer matrix. Biodegradation test revealed a reduction in the mass of the composites after a 3- month burial period which was more pronounced after a 30-day test period indicating that the composite is more environmentally friendly. The highest degradation rate was observed at 20wt% CCSB-LDPE composite giving a 15% reduction after 90days. Result from the water imbibition test indicated no increase in the mass of the composites after immersion in water. This is an indication that the composite can be utilized in wet environments. Hence, from the findings, it is suggested that agro-wastes like rice husk and sugarcane bagasse be employed as fillers in the manufacture of plastics because they are cheaper and viable. Finally, the produced plastics would degrade when discarded.
    VL  - 7
    IS  - 3
    ER  - 

    Copy | Download

Author Information
  • Department of Pure and Industrial Chemistry, Nnamdi Azikiwe University, Awka, Nigeria

  • Department of Pure and Industrial Chemistry, Nnamdi Azikiwe University, Awka, Nigeria

  • Department of Pure and Industrial Chemistry, Nnamdi Azikiwe University, Awka, Nigeria

  • Department of Pure and Industrial Chemistry, Nnamdi Azikiwe University, Awka, Nigeria

  • Sections