Evaluation of Laminated Composites Reinforced by High-performance Kevlar Filaments with Variable SiO2: Mechanical, Morphological & Thermal Tests

Received: 12 August 2020    Accepted: 24 August 2020    Published: 16 September 2020
Views:       Downloads:

Share This Article

Abstract

In contemporary years, a necessity to produce satisfactory and progressive modules for engineering roles have been expanded rapidly. Laminated fiber-strengthened composite substances have well-made candidature for satisfying those factors with huge applications in nearly all regions of engineering and technology. Glass, Carbon, and aramid fibers are using extensively for the manufacturing of fiber-bolstered polymer composites. Kevlar is the highly accepted aramid fiber having an extended chain of strong, ring-like aromatic molecules. Superior temperature and shock-resistant aspects make kevlar the maximum promising antiballistic fabric with balance at elevated temperatures. It is extensively used for human body armor panels for light-weight army vehicles, bulletproof jackets, and fireproof bodysuits, and in aerospace industries, etc. In this work, we tested the tensile, flexural, and impacts strength of kevlar 49 (K-49) fiber-reinforced polymer complex. We additionally characterized its DTG/TG test, FTIR test, and SEM analysis for a definite and reliable notion of it. The composite samples used on this work had been organized with the aid of using hand lay-up procedure. All Mechanical characterizations had been carried out according to the necessities of ASTM standards. In this study, highest tensile strength and elastic modulus was observed for 5*% milled silica and lowest for composite with 0% silica. Composite C4 of 2% silica shows the maximum hardness in both Leeb rebound and Vickers micro hardness method (320.1HV, 447.8HRC). DTG curves of composites show that at 378.8°C, and 355.5°C the rate of degradation of the composite was 559 µg/min, and 58.5µg/min for composite C1, and C7 respectively. However, the findings were supported by FTIR and SEM images analysis.

DOI 10.11648/j.cm.20200402.11
Published in Composite Materials (Volume 4, Issue 2, December 2020)
Page(s) 15-24
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2024. Published by Science Publishing Group

Keywords

Kevlar, Laminated Composite, Tensile Strength, Flexural Strength, Water Absorption, Hardness, FTIR, SEM

References
[1] Sathishkumar, T., Satheeshkumar, S. and Naveen, J. Glass fiber-reinforced polymer composites–a review. Journal of Reinforced Plastics and Composites, 33, 13 (2014), 1258-1275.
[2] Roberts, G. D., Pereira, J. M., Braley, M. S., Dorer, J. D. and Watson, W. R. Design and testing of braided composite fan case materials and components (2009).
[3] Tham, C., Tan, V. and Lee, H.-P. Ballistic impact of a KEVLAR® helmet: Experiment and simulations. International Journal of Impact Engineering, 35, 5 (2008), 304-318.
[4] Ebrahimnezhad-Khaljiri, H., Eslami-Farsani, R. and Akbarzadeh, E. Effect of interlayer hybridization of carbon, Kevlar, and glass fibers with oxidized polyacrylonitrile fibers on the mechanical behaviors of hybrid composites. Proceedings of the Institution of Mechanical Engineers, Part C: Journal of Mechanical Engineering Science, 234, 9 (2020), 1823-1835.
[5] Walters, W. and Scott, B. High velocity penetration of a Kevlar reinforced laminate. Proc. Of the 22nd SAMPLE Int’l Tech. Conf. (1990) 1078-1091.
[6] Bandaru, A. K., Chavan, V. V., Ahmad, S., Alagirusamy, R. and Bhatnagar, N. Ballistic impact response of Kevlar® reinforced thermoplastic composite armors. International Journal of Impact Engineering, 89 (2016), 1-13.
[7] Park, B., Lee, W., Lee, E., Min, S. H. and Kim, B.-S. Highly tunable interfacial adhesion of glass fiber by hybrid multilayers of graphene oxide and aramid nanofiber. ACS applied materials & interfaces, 7, 5 (2015), 3329-3334.
[8] Lian, M., Fan, J., Shi, Z., Li, H. and Yin, J. Kevlar®-functionalized graphene nanoribbon for polymer reinforcement. Polymer, 55, 10 (2014), 2578-2587.
[9] Jin, F. L., Ma, C. J. and Park, S. J. Thermal and mechanical interfacial properties of epoxy composites based on functionalized carbon nanotubes. Materials Science and Engineering: A, 528, 29-30 (2011), 8517-8522.
[10] Zhu, L., Jin, F.-L. and Park, S.-J. Thermal stability and fracture toughness of epoxy resins modified with epoxidized castor oil and Al2O3 nanoparticles. Bull Korean Chem Soc, 33 (2012), 2513.
[11] Mourad, A.-H. I., Idrisi, A. H., Zaaroura, N., Sherif, M. M. and Fouad, H. Damage assessment of nanofiller-reinforced woven kevlar KM2plus/Epoxy resin laminated composites. Polymer Testing (2020), 106501.
[12] Kumar, S., Gupta, D. S., Singh, I. and Sharma, A. Behavior of kevlar/epoxy composite plates under ballistic impact. Journal of Reinforced Plastics and Composites, 29, 13 (2010), 2048-2064.
[13] Bigdilou, M., Eslami-Farsani, R., Ebrahimnezhad-Khaljiri, H. and Mohammadi, M. A. Experimental assessment of adding carbon nanotubes on the impact properties of Kevlar-ultrahigh molecular weight polyethylene fibers hybrid composites. Journal of Industrial Textiles (2020).
[14] Sharma, S., Pathak, A. K., Singh, V. N., Teotia, S., Dhakate, S. and Singh, B. Excellent mechanical properties of long multiwalled carbon nanotube bridged Kevlar fabric. Carbon, 137 (2018), 104-117.
[15] Sharma, S., Kumar, V., Pathak, A. K., Yokozeki, T., Yadav, S. K., Singh, V. N., Dhakate, S. and Singh, B. P. Design of MWCNT bucky paper reinforced PANI–DBSA–DVB composites with superior electrical and mechanical properties. Journal of Materials Chemistry C, 6, 45 (2018), 12396-12406.
[16] Al-Qabandi, O., De Silva, A., Al-Enezi, S. and Bassyouni, M. Synthesis, fabrication and mechanical characterization of reinforced epoxy and polypropylene composites for wind turbine blades. Journal of Reinforced Plastics and Composites, 33, 24 (2014), 2287-2299.
[17] Tseng, H.-C., Chang, R.-Y. and Hsu, C.-H. Numerical prediction of fiber orientation and mechanical performance for short/long glass and carbon fiber-reinforced composites. Composites Science and Technology, 144 (2017), 51-56.
[18] Sprenger, S. Improved performance of glass and carbon fiber-reinforced composites by using nanosilica in the fiber sizing. (2017).
[19] Tate, J. S., Akinola, A. T., Espinoza, S., Gaikwad, S., Kannabiran Vasudevan, D. K., Sprenger, S. and Kumar, K. Tension–tension fatigue performance and stiffness degradation of nanosilica-modified glass fiber-reinforced composites. Journal of Composite Materials, 52, 6 (2018), 823-834.
[20] Jeffery, M. and Williams, J. DuPont-NASCAR Marketing. Kellogg School of Management Cases (2017).
[21] Hossain, M. S., Hossain, M. S., Rahman, M. M., Chowdhury, A. and Khan, R. A. Fabrication and characterization of Kevlar fiber reinforced polypropylene based composite for civil applications. Adv Mater, 7, 4 (2018), 105-110.
[22] Gupta, M. and Srivastava, R. Mechanical, thermal and water absorption properties of hybrid sisal/jute fiber reinforced polymer composite (2016).
[23] Hashim, N., Abdul Majid, D. L., Zahari, R. and Yidris, N. Tensile properties of woven Carbon/Kevlar reinforced epoxy hybrid composite. Trans Tech Publ. (2017).
[24] Dorado, A. A., Peralta, E. K., Carpio, E. V., Lozada, E. P. and Elepaño, A. R. Biodegradable corn starch/silica nanocomposite sheets for food packaging applications. Trans Tech Publ. (2017).
[25] Gorrepati, S. R., Sharma, B., Vates, U., Phanden, R. K., Mussada, E. K., Saha, S., Mohammed, A., Bannaravuri, P. K. and Rao, G. B. Fabrication and bend testing of DHAK fiber composites. Materials Today: Proceedings (2020).
[26] Chetty, S. The structural integrity of nanoclay filled epoxy polymer under cyclic loading. 2017.
[27] Khodadadi, A., Liaghat, G., Ahmadi, H., Bahramian, A. R. and Razmkhah, O. Impact response of Kevlar/rubber composite. Composites Science and Technology, 184 (2019), 107880.
[28] Bhanupratap, R. Study on characterization and sorption behavior of jute reinforced epoxy composite: Hybridization effect of Kevlar fabric. Materials Today: Proceedings, 27 (2020), 2017-2021.
[29] Miah, M. Y., Bhattacharjee, S., Begum, A., Bhowmik, S., Islam, M. S., Gafur, A. and Islam, M. S. Fabrication and Characterization of Differently Laminated Jute Mat-PVC Composites. MAYFEB Journal of Materials Science, 1 (2017).
Author Information
  • Department of Applied Chemistry and Chemical Engineering, University of Dhaka, Dhaka, Bangladesh; Bangladesh Council of Scientific and Industrial Research (BCSIR), Dhaka, Bangladesh

  • Department of Aeronautical Engineering, Military Institute of Science and Technology (MIST), Dhaka, Bangladesh

  • Bangladesh Council of Scientific and Industrial Research (BCSIR), Dhaka, Bangladesh; Department of Microbiology, Noakhali Science and Technology University, Noakhali, Bangladesh

  • Department of Applied Chemistry and Chemical Engineering, University of Dhaka, Dhaka, Bangladesh

  • Department of Applied Chemistry and Chemical Engineering, University of Dhaka, Dhaka, Bangladesh; Department of Chemistry, Gaibandha Mohilla College, Gaibandha, Bangladesh

  • Bangladesh Council of Scientific and Industrial Research (BCSIR), Dhaka, Bangladesh

  • Department of Applied Chemistry and Chemical Engineering, University of Dhaka, Dhaka, Bangladesh

Cite This Article
  • APA Style

    Md. Sahab Uddin, Md. Shariful Islam, Farjana Showline Chaity, Md. Ali Akbar, Shahin Akand, et al. (2020). Evaluation of Laminated Composites Reinforced by High-performance Kevlar Filaments with Variable SiO2: Mechanical, Morphological & Thermal Tests. Composite Materials, 4(2), 15-24. https://doi.org/10.11648/j.cm.20200402.11

    Copy | Download

    ACS Style

    Md. Sahab Uddin; Md. Shariful Islam; Farjana Showline Chaity; Md. Ali Akbar; Shahin Akand, et al. Evaluation of Laminated Composites Reinforced by High-performance Kevlar Filaments with Variable SiO2: Mechanical, Morphological & Thermal Tests. Compos. Mater. 2020, 4(2), 15-24. doi: 10.11648/j.cm.20200402.11

    Copy | Download

    AMA Style

    Md. Sahab Uddin, Md. Shariful Islam, Farjana Showline Chaity, Md. Ali Akbar, Shahin Akand, et al. Evaluation of Laminated Composites Reinforced by High-performance Kevlar Filaments with Variable SiO2: Mechanical, Morphological & Thermal Tests. Compos Mater. 2020;4(2):15-24. doi: 10.11648/j.cm.20200402.11

    Copy | Download

  • @article{10.11648/j.cm.20200402.11,
      author = {Md. Sahab Uddin and Md. Shariful Islam and Farjana Showline Chaity and Md. Ali Akbar and Shahin Akand and M. A. Gafur and A. M. Sarwaruddin Chowdhury},
      title = {Evaluation of Laminated Composites Reinforced by High-performance Kevlar Filaments with Variable SiO2: Mechanical, Morphological & Thermal Tests},
      journal = {Composite Materials},
      volume = {4},
      number = {2},
      pages = {15-24},
      doi = {10.11648/j.cm.20200402.11},
      url = {https://doi.org/10.11648/j.cm.20200402.11},
      eprint = {https://download.sciencepg.com/pdf/10.11648.j.cm.20200402.11},
      abstract = {In contemporary years, a necessity to produce satisfactory and progressive modules for engineering roles have been expanded rapidly. Laminated fiber-strengthened composite substances have well-made candidature for satisfying those factors with huge applications in nearly all regions of engineering and technology. Glass, Carbon, and aramid fibers are using extensively for the manufacturing of fiber-bolstered polymer composites. Kevlar is the highly accepted aramid fiber having an extended chain of strong, ring-like aromatic molecules. Superior temperature and shock-resistant aspects make kevlar the maximum promising antiballistic fabric with balance at elevated temperatures. It is extensively used for human body armor panels for light-weight army vehicles, bulletproof jackets, and fireproof bodysuits, and in aerospace industries, etc. In this work, we tested the tensile, flexural, and impacts strength of kevlar 49 (K-49) fiber-reinforced polymer complex. We additionally characterized its DTG/TG test, FTIR test, and SEM analysis for a definite and reliable notion of it. The composite samples used on this work had been organized with the aid of using hand lay-up procedure. All Mechanical characterizations had been carried out according to the necessities of ASTM standards. In this study, highest tensile strength and elastic modulus was observed for 5*% milled silica and lowest for composite with 0% silica. Composite C4 of 2% silica shows the maximum hardness in both Leeb rebound and Vickers micro hardness method (320.1HV, 447.8HRC). DTG curves of composites show that at 378.8°C, and 355.5°C the rate of degradation of the composite was 559 µg/min, and 58.5µg/min for composite C1, and C7 respectively. However, the findings were supported by FTIR and SEM images analysis.},
     year = {2020}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Evaluation of Laminated Composites Reinforced by High-performance Kevlar Filaments with Variable SiO2: Mechanical, Morphological & Thermal Tests
    AU  - Md. Sahab Uddin
    AU  - Md. Shariful Islam
    AU  - Farjana Showline Chaity
    AU  - Md. Ali Akbar
    AU  - Shahin Akand
    AU  - M. A. Gafur
    AU  - A. M. Sarwaruddin Chowdhury
    Y1  - 2020/09/16
    PY  - 2020
    N1  - https://doi.org/10.11648/j.cm.20200402.11
    DO  - 10.11648/j.cm.20200402.11
    T2  - Composite Materials
    JF  - Composite Materials
    JO  - Composite Materials
    SP  - 15
    EP  - 24
    PB  - Science Publishing Group
    SN  - 2994-7103
    UR  - https://doi.org/10.11648/j.cm.20200402.11
    AB  - In contemporary years, a necessity to produce satisfactory and progressive modules for engineering roles have been expanded rapidly. Laminated fiber-strengthened composite substances have well-made candidature for satisfying those factors with huge applications in nearly all regions of engineering and technology. Glass, Carbon, and aramid fibers are using extensively for the manufacturing of fiber-bolstered polymer composites. Kevlar is the highly accepted aramid fiber having an extended chain of strong, ring-like aromatic molecules. Superior temperature and shock-resistant aspects make kevlar the maximum promising antiballistic fabric with balance at elevated temperatures. It is extensively used for human body armor panels for light-weight army vehicles, bulletproof jackets, and fireproof bodysuits, and in aerospace industries, etc. In this work, we tested the tensile, flexural, and impacts strength of kevlar 49 (K-49) fiber-reinforced polymer complex. We additionally characterized its DTG/TG test, FTIR test, and SEM analysis for a definite and reliable notion of it. The composite samples used on this work had been organized with the aid of using hand lay-up procedure. All Mechanical characterizations had been carried out according to the necessities of ASTM standards. In this study, highest tensile strength and elastic modulus was observed for 5*% milled silica and lowest for composite with 0% silica. Composite C4 of 2% silica shows the maximum hardness in both Leeb rebound and Vickers micro hardness method (320.1HV, 447.8HRC). DTG curves of composites show that at 378.8°C, and 355.5°C the rate of degradation of the composite was 559 µg/min, and 58.5µg/min for composite C1, and C7 respectively. However, the findings were supported by FTIR and SEM images analysis.
    VL  - 4
    IS  - 2
    ER  - 

    Copy | Download

  • Sections