Growth of Zinc Oxide Nanocombs on Porous Silicon Layer by Thermal-Evaporation Method

Received: 15 February 2015    Accepted: 26 February 2015    Published: 08 March 2015
Views:       Downloads:

Share This Article

Abstract

Zinc oxide (ZnO) film was deposited on a porous silicon (PS) layer prepared by electrochemical etching through the thermal-evaporation method. ZnO nanocombs structure arrays were directly fabricated on the PS substrate through zinc powder evaporation, which uses a simple thermal-evaporation method without a catalyst. The ZnO nanocombs were highly oriented along the c-axis perpendicular to the PS layer. The average crystallite size of the PS and the ZnO nanocombs were 17.06 and 17.94 nm, respectively. The photoluminescence emission spectra of the ZnO nanocombs grown on the PS layer showed three emission peaks. The two peaks located at 387.5 and 605 nm were caused by the ZnO nanocombs, whereas the third peak located at 637.5 nm was caused by the PS layer. The ZnO nanocombs grown on the PS layer exhibited exceptional light trapping at wavelengths ranging from 400 to 1000 nm, which was expected to increase the efficiency of nano-electronic and nano-optical devices such as (solar cells).

DOI 10.11648/j.am.20150402.12
Published in Advances in Materials (Volume 4, Issue 2, April 2015)
Page(s) 30-35
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2024. Published by Science Publishing Group

Keywords

Zinc Oxide Film, Nanocombs, Porous Silicon Layer, Electrochemical Etching

References
[1] R.C. Pawar, J.S. Shaikh, A.A. Babar, P.M. Dhere, P.S. Patil, Sol. Energy 85 (2011) 1119.
[2] Z.Z. Ye, J.G. Lu, Y.Z. Zhang, Y.J. Zeng, L.L. Chen, F. Zhuge, G.D. Yuan, H.P. He, L.P. Zhu, J.Y. Huang, B.H. Zhao, Appl. Phys. Lett. 91 (2007) 113503.
[3] E.M. Wong, P.C. Searson, Appl. Phys. Lett. 74 (1999) 2939.
[4] L. Bahadur, M. Hamdani, J.F. Koenig, P. Chartier, Sol. Energ. Mater. 14 (1986) 107.
[5] Y.-J. Lee, D.S. Ruby, D.W. Peters, B.B. McKenzie, J.W.P. Hsu, Nano Lett. 8 (2008) 1501.
[6] L.T. Canham, Appl. Phys. Lett. 57 (1990) 1046.
[7] N. Koshida, H. Koyama, Mater. Res. Soc. Symp. 256 (1992) 219.
[8] H.-C. Hsu, C.-S. Cheng, C.-C. Chang, S. Yang, C.-S. Chang, W.-F. Hsieh, Nanotechnology 16 (2005) 297.
[9] C. Shaoqiang, Z. Jian, F. Xiao, W. Xiaohua, L. laiqiang, S. Yanling, X. Qingsong, W. Chang, Z. Jianzhong, Z. Ziqiang, Appl. Surf. Sci. 241 (2005) 384.
[10] O. Bisi, S. Ossicini, L. Pavesi, Surf. Sci. Rep. 38 (2000) 1.
[11] J.Y. Chen, K.W. Sun, Energy Mater. Sol. Cells 94 (2010) 930.
[12] K. Haga, P.S. Wijesena, H. Watanabe, Appl. Surf. Sci. 169-170 (2001) 504.
[13] C.H. Zang, Y.C. Liu, D.X. Zhao, J.Y. Zhang, D.Z. Shen, J. Nanosci. Nanotechnol. 10 (2010) 2370.
[14] S. Fujihara, C. Sasaki, T. Kimura, Appl. Surf. Sci. 180 (2001) 341.
[15] G.L. Harding, B. Window, E.C. Horrigan, Sol. Energ. Mater. 22 (1991) 69.
[16] H. Cai, H. Shen, Y. Yin, L. Lu, J. Shen, Z. Tang, Chem. Solids 70 (2009) 967.
[17] H.I. Abdulgafour, F.K.Yam, Z. Hassan, K. Al-Heuseen, M.J. JawadJ. Alloys Compd. 509 (2011) 5627.
[18] C.S. Lao, P.X. Gao, R.S. Yang, Y. Zhang, Y. Dai, Z.L. Wang, Chem. Phys. Lett. 417 (2005) 359.
[19] P.L. Ossicini S. L., Priolo F., Light emitting silicon for microphotonics, Springer-Verlag, Berlin Heidelberg, 2003.
[20] J. Nijs, S. Sivoththaman, J. Szlufcik, K. De Clercq, F. Duerinckx, E. Van Kerschaever, R. Einhaus, J. Poortmans, T. Vermeulen, R. Mertens, Sol. Energy Mater. Sol. Cells 48 (1997) 199.
[21] S. Faÿ, A. Shah, in: K. Ellmer, A. Klein, B. Rech (Eds.), Transparent Conductive Zinc Oxide, vol. 104, Springer Berlin Heidelberg, 2008, p. 235.
[22] M. Gabás, P. Díaz-Carrasco, F. Agulló-Rueda, P. Herrero, A.R. Landa-Cánovas, J.R. Ramos-Barrado, Sol. Energy Mater. Sol. Cells 95 (2011) 2327.
[23] J.J. Hassan, Z. Hassan, H. Abu-Hassan, J. Alloys Compd. 509 (2011) 6711.
[24] B.D. Cullity, Elements of X-ray Diffraction, Addison-Wesley, London, 1959.
[25] J.J. Yon, K. Barla, R. Herino, G. Bomchil, J. Appl. Phys. 62 (1987) 1042.
[26] C.-Y. Tsay, K.-S. Fan, S.-H. Chen, C.-H. Tsai, J. Alloys Compd. 495 (2010) 126.
[27] R. Ghosh, D. Basak, J. Appl. Phys. 96 (2004) 2689.
[28] D.-T. Phan, G.-S. Chung, Appl. Surf. Sci. 257 (2011) 3285.
[29] N. Gopalakrishnan, B.C. Shin, H.S. Lim, G.Y. Kim, Y.S. Yu, Phys. B (Amsterdam, Neth.) 376-377 (2006) 756.
[30] C.H. Chen, Y.F. Chen, Appl. Phys. Lett. 75 (1999) 2560.
[31] C.-F. Yu, C.-W. Sung, S.-H. Chen, S.-J. Sun, Appl. Surf. Sci. 256 (2009) 792.
[32] A. Umar, B. Karunagaran, E.-K. Suh, Y.B. Hahn, Nanotechnology 17 (2006) 4072.
[33] Y.L. Liu, Y.C. Liu, H. Yang, W.B. Wang, J.G. Ma, J.Y. Zhang, Y.M. Lu, D.Z. Shen, X.W. Fan, J. Phys. D: Appl. Phys. 36 (2003) 2705.
[34] D. Verma, F. Khan, S.N. Singh, P.K. Singh, Sol. Energy Mater. Sol. Cells 95 (2011) 30.
[35] R.E. Hummel, M.H. Ludwig, S.S. Chang, Solid State Commun. 93 (1995) 237.
[36] E. Kayahan, J. Lumin. 130 (2010) 1295.
[37] O.D. Jayakumar, V. Sudarsan, C. Sudakar, R. Naik, R.K. Vatsa, A.K. Tyagi, Scr. Mater. 62 (2010) 662.
[38] R. Prabakaran, M. Peres, T. Monteiro, E. Fortunato, R. Martins, I. Ferreira, J. Non-Cryst. Solids 354 (2008) 2181.
[39] X.L. Wu, S.J. Xiong, D.L. Fan, Y. Gu, X.M. Bao, Phys. Rev. B 62 (2000) 7759.
[40] D.E. Aspnes, J.B. Theeten, F. Hottier, Phys. Rev. B 20 (1979) 3292.
Author Information
  • Solar Energy Researches Department, Al-Nahrain Nanorenewable Energy Researches Center, Al-Nahrain University, Baghdad, Iraq

Cite This Article
  • APA Style

    Khaldun A. Salman. (2015). Growth of Zinc Oxide Nanocombs on Porous Silicon Layer by Thermal-Evaporation Method. Advances in Materials, 4(2), 30-35. https://doi.org/10.11648/j.am.20150402.12

    Copy | Download

    ACS Style

    Khaldun A. Salman. Growth of Zinc Oxide Nanocombs on Porous Silicon Layer by Thermal-Evaporation Method. Adv. Mater. 2015, 4(2), 30-35. doi: 10.11648/j.am.20150402.12

    Copy | Download

    AMA Style

    Khaldun A. Salman. Growth of Zinc Oxide Nanocombs on Porous Silicon Layer by Thermal-Evaporation Method. Adv Mater. 2015;4(2):30-35. doi: 10.11648/j.am.20150402.12

    Copy | Download

  • @article{10.11648/j.am.20150402.12,
      author = {Khaldun A. Salman},
      title = {Growth of Zinc Oxide Nanocombs on Porous Silicon Layer by Thermal-Evaporation Method},
      journal = {Advances in Materials},
      volume = {4},
      number = {2},
      pages = {30-35},
      doi = {10.11648/j.am.20150402.12},
      url = {https://doi.org/10.11648/j.am.20150402.12},
      eprint = {https://download.sciencepg.com/pdf/10.11648.j.am.20150402.12},
      abstract = {Zinc oxide (ZnO) film was deposited on a porous silicon (PS) layer prepared by electrochemical etching through the thermal-evaporation method. ZnO nanocombs structure arrays were directly fabricated on the PS substrate through zinc powder evaporation, which uses a simple thermal-evaporation method without a catalyst. The ZnO nanocombs were highly oriented along the c-axis perpendicular to the PS layer. The average crystallite size of the PS and the ZnO nanocombs were 17.06 and 17.94 nm, respectively. The photoluminescence emission spectra of the ZnO nanocombs grown on the PS layer showed three emission peaks. The two peaks located at 387.5 and 605 nm were caused by the ZnO nanocombs, whereas the third peak located at 637.5 nm was caused by the PS layer. The ZnO nanocombs grown on the PS layer exhibited exceptional light trapping at wavelengths ranging from 400 to 1000 nm, which was expected to increase the efficiency of nano-electronic and nano-optical devices such as (solar cells).},
     year = {2015}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Growth of Zinc Oxide Nanocombs on Porous Silicon Layer by Thermal-Evaporation Method
    AU  - Khaldun A. Salman
    Y1  - 2015/03/08
    PY  - 2015
    N1  - https://doi.org/10.11648/j.am.20150402.12
    DO  - 10.11648/j.am.20150402.12
    T2  - Advances in Materials
    JF  - Advances in Materials
    JO  - Advances in Materials
    SP  - 30
    EP  - 35
    PB  - Science Publishing Group
    SN  - 2327-252X
    UR  - https://doi.org/10.11648/j.am.20150402.12
    AB  - Zinc oxide (ZnO) film was deposited on a porous silicon (PS) layer prepared by electrochemical etching through the thermal-evaporation method. ZnO nanocombs structure arrays were directly fabricated on the PS substrate through zinc powder evaporation, which uses a simple thermal-evaporation method without a catalyst. The ZnO nanocombs were highly oriented along the c-axis perpendicular to the PS layer. The average crystallite size of the PS and the ZnO nanocombs were 17.06 and 17.94 nm, respectively. The photoluminescence emission spectra of the ZnO nanocombs grown on the PS layer showed three emission peaks. The two peaks located at 387.5 and 605 nm were caused by the ZnO nanocombs, whereas the third peak located at 637.5 nm was caused by the PS layer. The ZnO nanocombs grown on the PS layer exhibited exceptional light trapping at wavelengths ranging from 400 to 1000 nm, which was expected to increase the efficiency of nano-electronic and nano-optical devices such as (solar cells).
    VL  - 4
    IS  - 2
    ER  - 

    Copy | Download

  • Sections