A Low Temperature Manufactured Portland Cement Clinker from Pulverized Waste of Fly Ash

Received: 21 April 2020    Accepted: 18 May 2020    Published: 28 June 2020
Views:       Downloads:

Share This Article

Abstract

The possibility to produce both environmentally and friendly cement exclusively or solely from industrial byproducts such as pulverized fly ash (PFa) was investigated. A low clinkering temperature was attained or acquired to produce cement. It is capable to gain high early and late strength on hydration. The optimum quantities of PFa and clinkering temperature were detected. The results indicated that the higher the clinkering temperature, the higher hydration reactivity of the cement. The optimum PFa content and clinkering temperature for synthesizing cement were found to be 35 wt. % and 1350°C, respectively. The production of cement with PFa at a low clinkering temperature can save energy and natural resources consumption, landfills disposal cost and also can reduce CO2↑ emission. The formed major phases in presence of PFa are more or less the same as those of the blank as experimentally achieved and approved by the compressive strength. As the PFa content increased, the free lime contents decreased, and also the firing or clinkering temperature decreased. The optimum PFa content must not exceed than 35 wt. %, and any further increase of Pfa resulted in adverse effects on all characteristics of the produced clinker.

DOI 10.11648/j.ijmsa.20200902.12
Published in International Journal of Materials Science and Applications (Volume 9, Issue 2, March 2020)
Page(s) 34-39
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2024. Published by Science Publishing Group

Keywords

Cement, Fly Ash, Clinkering Temperature, Phases, Hydration, Free Lime, Strength, XRF

References
[1] Zhang, H.; Hu, J.; Qi, Y.; Li, C.; Chen, J.; Wang, X.; He, J.; Wang, S.; Hao, J.; Zhang, L., Zhang, Y., Li, R; Wang, S.; Chai, F (2017), Emission characterization, environmental impact, and control measure of PM2.5 emitted from agricultural crop residue burning in China. Journal of Cleaner Production, 149: 629-635. https://doi.org/10.1016/j.jclepro.2017.02.092
[2] Olgun A; Erdogan Y; Ayhan Y; Zeybek B (2005), Developments of ceramic tiles from coal fly ash and tincal ore waste, Ceramics International, 31, 1, 153-158. https://doi.org/10.1016/j.ceramint.2004.04.007
[3] Kumar S; Patil CP (2006), Estimation of resource savings due to fly ash utilization in road construction, Resources, Conserv. Recycling, 48, 2, 125-140. https://doi.org/10.1016/j.resconrec.2006.01.002
[4] Majchrzak-Kuceba I; Nowak W (2004), Thermal analysis of fly ash based zeolites, J. Thermal Analysis Calorim, 77, 125-131. https://doi.org/10.1023/B:JTAN.0000033195.15101.4e
[5] Moreno N; Querol X; Andrés JM; Stanton K; Towler M; Nugteren H; Janssen-Jurkovicov M; Jones R (2005), Physico-chemical characteristics of European pulverized coal combustion fly ashes, Fuel, 84, 1351–1363. https://doi.org/10.1016/j.fuel.2004.06.038
[6] Pacewska B; Blonkowski G; Wilinska I (2008), Studies on the pozzolanic and hydraulic properties of fly ashes in model systems, 94, 1, 2, 469–476. https://doi.org/10.1007/s10973-008-9179-8
[7] Pacewska B; Blonkowski G; Wilinska I (2006), Investigations of the influence of different fly ashes on cement hydration, J. Therm. Anal. Cal., 86, 1, 1, 179–186. https://doi.org/10.1007/s10673-005-7136-7
[8] Lee SH; Sakai E; Daimon M; Bang WK (1999), Characterization of fly ash directly collected from electrostatic precipitator, Cem. Concr. Res. 29, 11, 1791–1797.
[9] Koukouzas NK; RZeng R; Perdikatsis V; Xu W; Kakaras EK 2006), Mineralogy and geochemistry of Greek and Chinese coal fly ash and elemental composition, Fuel, 85, 16, 2301-2309. https://doi.org/10.1016/j.fuel.2006.02.019
[10] Darweesh, H.H.M. (2012), Setting, hardening and Strength properties of cement pastes with zeolite alone or in combination with slag, InterCeram International (Intern. Cer. Review), Germany, Vol. 1, 2012, 52-57.
[11] Ramamurthy K; Harikrishnan KI (2006), Influence of binders on properties of sintered fly ash aggregate, Cem. Concr. Compos., 28, 1, 33-38. https://doi.org/10.1016/j.cemconcomp.2005.06.005
[12] Canpolat F; Yilmaz K; Kose MM; Sumer M: Yurdusev MA (2004), Use of zeolite, coal bottom ash and fly ash as replacement materials in cement production, Cem. Concr. Res., 34, 5, 731-735. https://doi.org/10.1016/S0008-8846(03)00063-2
[13] Li B; Liang W; He Z (2002), Study on high-strength composite portland cement with a larger amount of industrial wastes, Cem. Concr. Res., 32, 8, 1341-1344.. https://doi.org/10.1016/S0008-8846(02)00804-9
[14] Tangpagasit J; Cheerarot R; Jaturapitakkul C; Kiattikomol K (2005), Packing effect and pozzolanic reaction of fly ash in mortar, Cement Concrete Res., 35, 1145-1151. https://doi.org/10.1016/j.cemconres.2004.09.030
[15] Blanco F; Garcia MP; JAyala J; Mayoral G; Garcia MA (2006), The effect of mechanically and chemically activated fly ashes on mortar properties, Fuel, 85, 2018-2026. https://doi.org/10.1016/j.fuel.2006.03.031
[16] Darweesh, HHM (2005), Effect of the combination of some pozzolanic wastes on the properties of Portland cement pastes, iiC L'industria italiana del Cemento, Italy, 808, 298-311.
[17] Darweesh, HHM (2017), Mortar Composites Based on Industrial Wastes, Intern. J. of Mater. Lifetime, 3, 1, 1-8. DOI:10.12691/ijml-3-1-1.
[18] Fan WJ; Wang XY; Park KP (2015), Evaluation of the Chemical and Mechanical Properties of Hardening High Calcium Fly Ash Blended Concrete, Materials, 8, 5933-5952.
[19] Mukherjee MK; Hegde SB; Somani AR (2002), Burnability improvement and raw mix optimization by addition of fly ash, Zem. Kalk Gips, 55, 2, 6-69.
[20] Komljenovi M; Petrašinović-Stoikanović Li; Baščarevi Z; Jovanović Rosić N (2009), Fly ash as the potential raw mixture component for Portland cement clinker synthesis, Journal of Thermal Analysis and Calorimetry, 96, 2, 363–368. https://doi.org/10.1007/s10973-008-8951-0
[21] Taylor, TFW (1997), Cement Chemistry, Academic Press Ltd., London, (2nd ed.) Google Scholar
[22] Darweesh, HHM; Abo-El-Suoud MR (2015), Quaternary cement composites from industrial byproducts to avoid the environmental pollution, J. EC-Chemistry, 2, 1, 78-91.
[23] Darweesh, HHM (2013), Hydration, Strength Development and Sulphate Attack of Some Cement Composites, World Applied Sciences Journal, 23 (2): 137-144. ISSN: 1818-4952,
[24] Hewlett PC; Liska M (2017), Lea’s Chemistry of Cement and Concrete, 5th ed., Edward Arnold Ltd., London, England. Google Scholar
[25] Wu K; ShiH; Guo X (2011), Utilization of municipal solid waste incineration fly ash for sulfoaluminate cement clinker production. Waste Manage, 31:2001–2008. https://doi.org/10.1016/j.wasman.2011.04.022
[26] ASTM- Standards-C114-77 (1978), Standard methods for chemical analysis of hydraulic cement, 87-127.
[27] ASTM Standards, C618-05 (2005), Standard Specification for coal fly ash and raw or calcined natural pozzolan for use in concrete.
[28] Darweesh HHM; Youssef H (2014), Preparation of 11-إ Al-substituted Tobermorite from Egyptian Trachyte Rock and its Effect on the Specific Propertiesof Portland Cement, InterCeram International (Int. Ceram. Review), 07–08, 358-362. https://doi.org/10.1007/BF03401084
[29] ASTM-Standards, C170-90 (1993), Standard Test Method for Compressive Strength of Dimension Stone, 828-830.
[30] Bhatty JI; Gajda J; Miller FM (2003), Commercial Demonstration of High-Carbon Fly Ash Technology in Cement Manufacturing, Intern. ash utilization Symp.
[31] Darweesh HHM (2020), Characteristics of Portland Cement Pastes Blended with Silica Nanoparticles, To Chemistry Journal, 5, 1-14. http://purkh.com/index.php/tochem
[32] El-Didamony H; Radwan A; Khattab I; El-Alfi SA; Mohammed MS (2014), Characteristics of sulphate resistant cement pastes containing different ratios of belite cement phase”, Journal of Engineering And Technology Research 2, 4, 52-62.
[33] Abd-El-Aziz MA; Heikal M (2009), Characteristics and durability of cements containing fly ash and limestone subjected to Carons’s lake water”, Advances in Cement Research 21 (3), 91-99. https://doi.org/10.1680/adcr.2007.00025
[34] Abd-El-Aziz MA; Heikal M (2013), Behavior of composite cement pastes containing micro silica and fly ash at elevated temperatures, Advances in Cement Research 21 (3), 91-99. https://doi.org/10.1680/adcr.2007.00025
[35] El-Didamony H; Heikal M; Shoaib M (2000), Homra pozzolanic cement, Silic Ind 65 (3- 4, 39-43.
[36] El-Didamony H; Darweesh HHM; Mostafa RA (2008), Characteristics of pozzolanic cement pastes Part I: Physico-mechanical properties” Sil. Ind. (Cer. Sci. & Techn.), Belgium, 73, Nr. 11-12, 193-200.
[37] Darweesh HHM (2017), Geopolymer cements from slag, fly ash and silica fume activated with sodium hydroxide and water glass, Interceram International”, 6, 1, 226-231. https://doi.org/10.1007/BF03401216
Author Information
  • Refractories, Ceramics and Building Materials Department, National Research Centre, Cairo, Egypt

Cite This Article
  • APA Style

    Hassan Hassanien Mohamed Darweesh. (2020). A Low Temperature Manufactured Portland Cement Clinker from Pulverized Waste of Fly Ash. International Journal of Materials Science and Applications, 9(2), 34-39. https://doi.org/10.11648/j.ijmsa.20200902.12

    Copy | Download

    ACS Style

    Hassan Hassanien Mohamed Darweesh. A Low Temperature Manufactured Portland Cement Clinker from Pulverized Waste of Fly Ash. Int. J. Mater. Sci. Appl. 2020, 9(2), 34-39. doi: 10.11648/j.ijmsa.20200902.12

    Copy | Download

    AMA Style

    Hassan Hassanien Mohamed Darweesh. A Low Temperature Manufactured Portland Cement Clinker from Pulverized Waste of Fly Ash. Int J Mater Sci Appl. 2020;9(2):34-39. doi: 10.11648/j.ijmsa.20200902.12

    Copy | Download

  • @article{10.11648/j.ijmsa.20200902.12,
      author = {Hassan Hassanien Mohamed Darweesh},
      title = {A Low Temperature Manufactured Portland Cement Clinker from Pulverized Waste of Fly Ash},
      journal = {International Journal of Materials Science and Applications},
      volume = {9},
      number = {2},
      pages = {34-39},
      doi = {10.11648/j.ijmsa.20200902.12},
      url = {https://doi.org/10.11648/j.ijmsa.20200902.12},
      eprint = {https://download.sciencepg.com/pdf/10.11648.j.ijmsa.20200902.12},
      abstract = {The possibility to produce both environmentally and friendly cement exclusively or solely from industrial byproducts such as pulverized fly ash (PFa) was investigated. A low clinkering temperature was attained or acquired to produce cement. It is capable to gain high early and late strength on hydration. The optimum quantities of PFa and clinkering temperature were detected. The results indicated that the higher the clinkering temperature, the higher hydration reactivity of the cement. The optimum PFa content and clinkering temperature for synthesizing cement were found to be 35 wt. % and 1350°C, respectively. The production of cement with PFa at a low clinkering temperature can save energy and natural resources consumption, landfills disposal cost and also can reduce CO2↑ emission. The formed major phases in presence of PFa are more or less the same as those of the blank as experimentally achieved and approved by the compressive strength. As the PFa content increased, the free lime contents decreased, and also the firing or clinkering temperature decreased. The optimum PFa content must not exceed than 35 wt. %, and any further increase of Pfa resulted in adverse effects on all characteristics of the produced clinker.},
     year = {2020}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - A Low Temperature Manufactured Portland Cement Clinker from Pulverized Waste of Fly Ash
    AU  - Hassan Hassanien Mohamed Darweesh
    Y1  - 2020/06/28
    PY  - 2020
    N1  - https://doi.org/10.11648/j.ijmsa.20200902.12
    DO  - 10.11648/j.ijmsa.20200902.12
    T2  - International Journal of Materials Science and Applications
    JF  - International Journal of Materials Science and Applications
    JO  - International Journal of Materials Science and Applications
    SP  - 34
    EP  - 39
    PB  - Science Publishing Group
    SN  - 2327-2643
    UR  - https://doi.org/10.11648/j.ijmsa.20200902.12
    AB  - The possibility to produce both environmentally and friendly cement exclusively or solely from industrial byproducts such as pulverized fly ash (PFa) was investigated. A low clinkering temperature was attained or acquired to produce cement. It is capable to gain high early and late strength on hydration. The optimum quantities of PFa and clinkering temperature were detected. The results indicated that the higher the clinkering temperature, the higher hydration reactivity of the cement. The optimum PFa content and clinkering temperature for synthesizing cement were found to be 35 wt. % and 1350°C, respectively. The production of cement with PFa at a low clinkering temperature can save energy and natural resources consumption, landfills disposal cost and also can reduce CO2↑ emission. The formed major phases in presence of PFa are more or less the same as those of the blank as experimentally achieved and approved by the compressive strength. As the PFa content increased, the free lime contents decreased, and also the firing or clinkering temperature decreased. The optimum PFa content must not exceed than 35 wt. %, and any further increase of Pfa resulted in adverse effects on all characteristics of the produced clinker.
    VL  - 9
    IS  - 2
    ER  - 

    Copy | Download

  • Sections