The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate

Tien-Chai Lin; Wen-Chang Huang; Fu-Chun Tsai

doi:doi:10.11648/j.ijmsa.20140305.21

| Peer-Reviewed

The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate

Tien-Chai Lin, Wen-Chang Huang, Fu-Chun Tsai

Published in International Journal of Materials Science and Applications (Volume 3, Issue 5)

Received: 29 August 2014 Accepted: 15 September 2014 Published: 30 September 2014

Views: Downloads:

Download PDF

Share This Article

Twitter
Linked In
Facebook

Abstract

The triple-layered transparent conductive oxide thin films, AZO/Mo/AZO (OMO) structure, is present in the paper. The OMO film is deposited on polycarbonate (PC) substrates by a co-sputtering process at room temperature. Metal Mo is chosen because of its chemical stable and low resistivity. The OMO film shows a great reduction of resistivity through the addition of Mo layer. The dependence of the AZO thickness of the electro-optical characteristic to the OMO film is also discussed. A best figure of merit (FOM) of 1.56 × 10-5 -1 with a sheet resistance of 530 Ω/□ and average transmittance of 62% is found at the OMO film of 130 nm thickness. At this condition, the AZO film shows a low resistivity due to its excellent crystallinity.

Published in	International Journal of Materials Science and Applications (Volume 3, Issue 5)
DOI	10.11648/j.ijmsa.20140305.21
Page(s)	205-209
Creative Commons	This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.
Copyright	Copyright © The Author(s), 2024. Published by Science Publishing Group

Keywords

Transparent Conductive Oxide, ZnO, Mo, Sheet Resistance, Transmittance

References

[1]	M. Purica, E. Budianu, E. Rusu, M. Danila, R. Gavrila,”Optical and structural investigation of ZnO thin films prepared by chemical vapor deposition (CVD)”, Thin Solid Films 403/404 (2002) 485-488.
[2]	G. A. Hirata, J. Mckittrik, T. Cheeks, J. M. Siqueiros, J. A. Diaz, O. Contreras, O. A. Lopez, “Synthesis and optelectronic characterization of gallium doped zinc oxide transparent electrodes”, Thin Solid Films 288 (1996) 29–31.
[3]	B. H. Choi, H. B. Im,” Optical and electrical properties of Ga2O3-doped ZnO films prepared by r.f. sputtering”, Thin Solid Films 193/194 (1990) 712–720.
[4]	T. Minami, H. Sato, H. Nanto, S. Takata,” High conductive and transparent silicon doped zinc oxide thin films prepared by RF magnetron sputtering”, Jpn. J. Appl. Phys. 125 (1986) L776.
[5]	T. C. Lin, W. F. Huang, W. C. Huang,” The effect of hydrogen annealing on the molybdenum doped ZnO thin film”, J Mater Sci: Mater Electro, 25 (2014) 2138-2142.
[6]	T. C. Lin, W.C. Huang, C. H. Liu. S. C. Chang,” Structural, electrical and optical properties of ZnO:AlF3 thin films deposited by RF magnetron sputtering”, Appl. Surf. Sci., 258/7 (2012)3302-3308.
[7]	F. Ruffino, E. Carria, S. Kimiagar, I. Crupi, F. Simone, M.G. Grimaldi,”Formation and evolution of nanoscale metal structures on ITO surface by nanosecond laser irradiations of thin Au and Ag films”, Sci. Adv. Mater. 4 (2012) 708-718.
[8]	F. Ruffino, I. Crupi, F. Simone, M.G. Grimaldi, Formation and evolution of self-organized Au nanorings on indium-tin-oxide surface”, Appl. Phys. Lett. 98 (2011) 023101-023103.
[9]	S. Song, T. Yang, M. Lv, Y. Li, Y. Xin, L. Jiang, Z. Wu, S. Han,“ Effect of Cu layer thickness on the structural, optical and electrical properties, of AZO/Cu/AZO tri-layer films”, Vacuum 85 (2010) 39-44.
[10]	D. Kim,” Low temperature deposition of transparent conducting ITO/Au/ITO films by reactive magnetron sputtering”, Appl. Surf. Sci. 256 (2010) 1774-1777.
[11]	J. A. Jeong, Y. S. Park, H. K. Kim, “ Comparison of electrical, optical, structural, and interface properties of IZO-Ag-IZO and IZO-Au-IZO multilayer electrodes for organic photovoltaics”, J. Appl. Phys. 107 (2010) 023111.
[12]	Y. S. Kim, J. H. Park, D. H. Choi, H. S. Jang, J. H. Lee, H. J. Park, J. I. Choi, D. H. Ju, J. Y. Lee, D. Kim,” ITO/Au/ITO multilayer thin films for transparent conducting electrode applications“ Appl. Surf. Sci. 254 (2007) 1524-1527.
[13]	L. Gong, J. Lu, Z. Ye, Transparent conductive Ga-doped ZnO/Cu multilayers prepared on polymer substrates at room temperature” Sol. Energ. Mat. Sol. C., 95 (2011)1826-1830.
[14]	D. R. Sahu, J. L. Huang, “Dependence of film thickness on the electrical and optical properties of ZnO–Cu–ZnO multilayers” Appl. Surf. Sci. 253 (2006) 915-918.
[15]	M. Bender, W. Seelig, C. Daube, H. Frankenberger, B. Ocker, J. Stollenwerk,“Dependence of oxygen flow on optical and electrical properties of DC-magnetron sputtered ITO films”, Thin Solid Films, 326(1998)72-77.
[16]	X. T. Hao, J. Ma, D. H. Zhang, T. L. Yang, H. L. Ma, Y. G. Yang, C. F. Cheng, J. Huang, Appl. Surf. Sci. 183 (2001) 137-142.
[17]	G. Leftheriotis, P. Yianoulis, D. Patrikios,” Deposition and optical properties of optimised ZnS/Ag/ZnS thin films for energy saving applications”, Thin Solid Films 306(1997) 92-99.
[18]	G. Haacke, J. Appl. Phys. 47 (1976) 4086-4089.

Cite This Article

Plain Text BibTeX RIS

APA Style

Tien-Chai Lin, Wen-Chang Huang, Fu-Chun Tsai. (2014). The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate. International Journal of Materials Science and Applications, 3(5), 205-209. https://doi.org/10.11648/j.ijmsa.20140305.21

Copy | Download

ACS Style

Tien-Chai Lin; Wen-Chang Huang; Fu-Chun Tsai. The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate. Int. J. Mater. Sci. Appl. 2014, 3(5), 205-209. doi: 10.11648/j.ijmsa.20140305.21

Copy | Download

AMA Style

Tien-Chai Lin, Wen-Chang Huang, Fu-Chun Tsai. The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate. Int J Mater Sci Appl. 2014;3(5):205-209. doi: 10.11648/j.ijmsa.20140305.21

Copy | Download

@article{10.11648/j.ijmsa.20140305.21,
  author = {Tien-Chai Lin and Wen-Chang Huang and Fu-Chun Tsai},
  title = {The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate},
  journal = {International Journal of Materials Science and Applications},
  volume = {3},
  number = {5},
  pages = {205-209},
  doi = {10.11648/j.ijmsa.20140305.21},
  url = {https://doi.org/10.11648/j.ijmsa.20140305.21},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ijmsa.20140305.21},
  abstract = {The triple-layered transparent conductive oxide thin films, AZO/Mo/AZO (OMO) structure, is present in the paper. The OMO film is deposited on polycarbonate (PC) substrates by a co-sputtering process at room temperature. Metal Mo is chosen because of its chemical stable and low resistivity. The OMO film shows a great reduction of resistivity through the addition of Mo layer. The dependence of the AZO thickness of the electro-optical characteristic to the OMO film is also discussed. A best figure of merit (FOM) of 1.56 × 10-5 -1 with a sheet resistance of 530 Ω/□ and average transmittance of 62% is found at the OMO film of 130 nm thickness. At this condition, the AZO film shows a low resistivity due to its excellent crystallinity.},
 year = {2014}
}

Copy | Download

TY  - JOUR
T1  - The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate
AU  - Tien-Chai Lin
AU  - Wen-Chang Huang
AU  - Fu-Chun Tsai
Y1  - 2014/09/30
PY  - 2014
N1  - https://doi.org/10.11648/j.ijmsa.20140305.21
DO  - 10.11648/j.ijmsa.20140305.21
T2  - International Journal of Materials Science and Applications
JF  - International Journal of Materials Science and Applications
JO  - International Journal of Materials Science and Applications
SP  - 205
EP  - 209
PB  - Science Publishing Group
SN  - 2327-2643
UR  - https://doi.org/10.11648/j.ijmsa.20140305.21
AB  - The triple-layered transparent conductive oxide thin films, AZO/Mo/AZO (OMO) structure, is present in the paper. The OMO film is deposited on polycarbonate (PC) substrates by a co-sputtering process at room temperature. Metal Mo is chosen because of its chemical stable and low resistivity. The OMO film shows a great reduction of resistivity through the addition of Mo layer. The dependence of the AZO thickness of the electro-optical characteristic to the OMO film is also discussed. A best figure of merit (FOM) of 1.56 × 10-5 -1 with a sheet resistance of 530 Ω/□ and average transmittance of 62% is found at the OMO film of 130 nm thickness. At this condition, the AZO film shows a low resistivity due to its excellent crystallinity.
VL  - 3
IS  - 5
ER  -

Copy | Download

Author Information

Tien-Chai Lin

Department of Electrical Engineering, Kun Shan University, Tainan, Taiwan
Wen-Chang Huang

Department of Electro-Optical Engineering, Kun Shan University, Tainan, Taiwan
Fu-Chun Tsai

Department of Electro-Optical Engineering, Kun Shan University, Tainan, Taiwan

Download PDF

Sections

Plain Text BibTeX RIS

APA Style

Tien-Chai Lin, Wen-Chang Huang, Fu-Chun Tsai. (2014). The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate. International Journal of Materials Science and Applications, 3(5), 205-209. https://doi.org/10.11648/j.ijmsa.20140305.21

Copy | Download

ACS Style

Tien-Chai Lin; Wen-Chang Huang; Fu-Chun Tsai. The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate. Int. J. Mater. Sci. Appl. 2014, 3(5), 205-209. doi: 10.11648/j.ijmsa.20140305.21

Copy | Download

AMA Style

Tien-Chai Lin, Wen-Chang Huang, Fu-Chun Tsai. The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate. Int J Mater Sci Appl. 2014;3(5):205-209. doi: 10.11648/j.ijmsa.20140305.21

Copy | Download

@article{10.11648/j.ijmsa.20140305.21,
  author = {Tien-Chai Lin and Wen-Chang Huang and Fu-Chun Tsai},
  title = {The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate},
  journal = {International Journal of Materials Science and Applications},
  volume = {3},
  number = {5},
  pages = {205-209},
  doi = {10.11648/j.ijmsa.20140305.21},
  url = {https://doi.org/10.11648/j.ijmsa.20140305.21},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ijmsa.20140305.21},
  abstract = {The triple-layered transparent conductive oxide thin films, AZO/Mo/AZO (OMO) structure, is present in the paper. The OMO film is deposited on polycarbonate (PC) substrates by a co-sputtering process at room temperature. Metal Mo is chosen because of its chemical stable and low resistivity. The OMO film shows a great reduction of resistivity through the addition of Mo layer. The dependence of the AZO thickness of the electro-optical characteristic to the OMO film is also discussed. A best figure of merit (FOM) of 1.56 × 10-5 -1 with a sheet resistance of 530 Ω/□ and average transmittance of 62% is found at the OMO film of 130 nm thickness. At this condition, the AZO film shows a low resistivity due to its excellent crystallinity.},
 year = {2014}
}

Copy | Download

TY  - JOUR
T1  - The Electro-Optical Characteristics of the AZO/Mo/AZO Transparent Conductive Film on PC Substrate
AU  - Tien-Chai Lin
AU  - Wen-Chang Huang
AU  - Fu-Chun Tsai
Y1  - 2014/09/30
PY  - 2014
N1  - https://doi.org/10.11648/j.ijmsa.20140305.21
DO  - 10.11648/j.ijmsa.20140305.21
T2  - International Journal of Materials Science and Applications
JF  - International Journal of Materials Science and Applications
JO  - International Journal of Materials Science and Applications
SP  - 205
EP  - 209
PB  - Science Publishing Group
SN  - 2327-2643
UR  - https://doi.org/10.11648/j.ijmsa.20140305.21
AB  - The triple-layered transparent conductive oxide thin films, AZO/Mo/AZO (OMO) structure, is present in the paper. The OMO film is deposited on polycarbonate (PC) substrates by a co-sputtering process at room temperature. Metal Mo is chosen because of its chemical stable and low resistivity. The OMO film shows a great reduction of resistivity through the addition of Mo layer. The dependence of the AZO thickness of the electro-optical characteristic to the OMO film is also discussed. A best figure of merit (FOM) of 1.56 × 10-5 -1 with a sheet resistance of 530 Ω/□ and average transmittance of 62% is found at the OMO film of 130 nm thickness. At this condition, the AZO film shows a low resistivity due to its excellent crystallinity.
VL  - 3
IS  - 5
ER  -

Copy | Download