Titanium oxide has been extensively used as a photocatalytic material because of its excellent UV light-responsive effect, high refractive index, and high chemical stability. TiO2 in anatase phase for applications in optical or electronic devices and photocatalysis has generally been used in the form of a thin film. The aim of this study was to prepare a stable TiO2 sol with high solid content. Therefore one can use less coating time to have a mono layer of TiO2 film on the substrate. In this study, TiCl4 was slowly added to the distilled water in an ice bath. Aqueous solution of sodium hydroxide was added to adjust the pH of the solution to between 8 and 12 to form titanium hydroxide gel. After aging for a period of time, the Ti(OH)4 gel was filtered and sufficiently washed. The filtered cake was repulped in water. Hydrochloric acid, as a catalyst for polycondensation, was slowly added to the solution with stirring. After poly-condensation reaction and crystallization, a transparent suspended TiO2 sol was formed. XRD results show that the crystalline phase was anatase. The suspended TiO2 particles were rhombus primary particles with the major axis ca. 20 nm and the minor axis ca. 5 nm. The sample prepared at pH 8 had the largest BET surface area of 141 cm3/g among all samples. The best preparation condition to have the smallest TiO2 particles are Ti: H = 1: 1 (atomic ratio), 10% solid content of TiO2, and hydroxypropyl cellulose with viscosity of 150-400 cps as a surfactant. The thin film was obtained by dip-coating the glass in TiO2 sol. Since the sol had high solid content, the coating time became less. The dip-coating on glass was less than three times to have one monolayer TiO2. The transparent TiO2 thin film had super-hydrophilicity after illumination by UV light.
| Published in | International Journal of Biochemistry, Biophysics & Molecular Biology (Volume 6, Issue 2) |
| DOI | 10.11648/j.ijbbmb.20210602.11 |
| Page(s) | 26-33 |
| Creative Commons |
This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited. |
| Copyright |
Copyright © The Author(s), 2024. Published by Science Publishing Group |
Titania, Photocatalysis, Sol-gel, Coating, Anatase
| [1] | Anpo M, Applications of titanium oxide photocatalysts and unique second-generation TiO2 photocatalysts able to operate under visible light irradiation for the reduction of environment toxins on a global scale, Stud Surf Sci Catal 130: 157-166 (2000). |
| [2] | Bischoff BL, Anderson MA, Peptization process in the sol-gel preparation of porous anatase (TiO2), Chem. Mater. 7: 1772-1778 (1995). |
| [3] | Chrysicopoulou P, Davazoglou D, Trapalis C, Kordas G, Optical properties of very thin (<100 nm) sol-gel TiO2 films, Thin Solid Films 323: 188-193 (1998). |
| [4] | Cheng H, Ma J, Zhao Z, Qi L, Hydrothermal preparation of uniform nanosize rutile and anatase particles, Chem. Mater. 7: 663-671 (1995). |
| [5] | Elfenthal L, Klein E, Rosendahl F, Process for the production of a fine particle titanium dioxide, Assignee: Kronos USA, Inc., U. S. Patent 5, 215, 580 (1993). |
| [6] | Foulger DL, Necini PG, Poeri S, Preparation of anatase titanium dioxide, Assignee: Tioxide Group Services Limited., U. S. Patent 5, 630, 995 (1997). |
| [7] | Haddow AJ, Oxidation of titanium tetrachloride to form titanium dioxide, Assignee: Tioxide Group Services Limited., U. S. Patent 5, 599, 519 (1997). |
| [8] | Kim DH, Anderson MA, Photoelectrocatalytic degradation of formic acid using a porous TiO2 thin-film electrode, Environ. Sci. Technol. 28: 479-483 (1994). |
| [9] | Kostelnik RJ, Wen FC, High solids anatase TiO2 slurries, Assignee: SCM Chemicals, Inc., U. S. Patent 5, 746, 819 (1998). |
| [10] | Lange RW, Sowman HG, Shaped and fired particles of TiO2, Assignee: Minnesota Mining and Manufacturing Company, U S Patent 4, 166, 147 (1979). |
| [11] | Li GL, Wang GH, Synthesis of nanometer-sized TiO2 particles by a mcroemulsion method, Nano Strustured Mater11: 663-668 (1999). |
| [12] | Li GL, Wang GH, Synthesis and characterization of rutile TiO2 nanowhiskers, J Mater Res 14: 3346-3354 (1999). |
| [13] | Mailhe-Randolph C, Mcevoy AJ, Gratzel M, Influence of precursors on the morphology and performance of TiO2 photoanodes, J Mater Sci 26: 3305-3308 (1991). |
| [14] | Man HD, Lee BH, Kim SJ, Jung CH, Lee JH, Park S, Preparation of ultrafine crystalline TiO2 powders from aqueous TiCl4 solution by precipitation, Japanese J App Phys 4603-4608 (1998). |
| [15] | Park HK, Kim DK, Kim CH, Effect of solvent on titania particle formation and morphology in thermal hydrolysis of TiCl4, J Am Ceram Soc 80: 743-749 (1997). |
| [16] | Park SD, Cho YH, Kim WW, Kim SJ, Understanding on homogeneous spontaneous precipitation for monodispersed of TiO2 ultrafine powders with rutile phase around room temperature, J Solid State Chem 146: 230-238 (1999). |
| [17] | Sakamoto M, Yokkaichi HO, Suzuka SK, Yokkaichi YY, Titania sol, Assignee: Ishihara Sangyo Kaisha, Ltd., U S Patent 4, 880, 703 (1991). |
| [18] | Sato G, Arima Y, Tanaka H, Hiraoka S, Titanium dioxide sol and process for preparation thereof, Assignee: Catalyst & Chemical Industries, Co., Ltd., US Patent 5, 403, 513 (1995). |
| [19] | Sopyan L, Watanabe M, Murasawa S, Hashimoto K, Fujishima A, An efficient TiO2 thin-film photocatalyst: photocatalytic properties in gas-phase acetaldehyde degradation, J Photochem Photobio A Chem 98: 79-86 (1996). |
| [20] | Takahashi H, Sakai A, Hattori M, Dendrite or asteriodal titanium dioxide nicro-particles, Assignee: Ishihara Sangyo Kaisha, Ltd., U S Patent 5, 536, 448 (1996). |
| [21] | Tunashima M, Muraoka K, Yamamoto K, Mikami M, Sasaki S, Stable anatase titanium dioxide and process for preparing the same, Assignee: Sakai Chemical Industry Co., Ltd., U S Patent 6, 113, 873 (2000). |
| [22] | Yasumori A, Ishizu K, Hayashi S, Okada K, Preparation of a TiO2 based multiple layer thin film photocatalyst, J Mater Chem 8: 2521-2524 (1998). |
| [23] | Mahshid S, Askar M, Ghamsar MS, Synthesis of TiO2 nanoparticles by hydrolysis and peptization of titanium isopropoxide solution, J Mater Processing Technol 189: 296-300 (2007). |
| [24] | Oskam G, Nellore A, Penn RL, Searson PC, The growth kinetics of TiO2 nanoparticles from titanium(IV) alkoxide at high water/titanium ratio, J Phys Chem B 107: 1734–1738 (2003). |
| [25] | Bui VKH, Tran VV, Moon JY, Park D, Lee YC, Titanium dioxide microscale and macroscale structures: a mini-review, Nanomater 10: 1190-1221 (2020). |
| [26] | Zhou W, Sun F, Pan K, Tian G, Jiang B, Ren Z, Tian C, Fu H, Well-ordered large-pore mesoporous anatase TiO2 with remarkably high thermal stability and improved crystallinity: Preparation, characterization, and photocatalytic performance. Adv Funct Mater 21: 1922–1930 (2011). |
| [27] | Rajaraman TS, Parikh SP, Gandhi VG, Black TiO2: A review of its properties and conflicting trends, Chem Eng J 389: 123918-123929 (2019). |
| [28] | Yoshihisa O, Kazuhito H, Fujishima A, Kinetic of photocatalyic reactions under extremely low-intensity UV illumination on titanium dioxide thin film, J Phys Chem A 101: 8057-8062 (1997). |
| [29] | Zhang Q, Gao L, Guo J, Effects of calcinations on the photocatalytic properties of nanosized TiO2 powders prepared by TiCl4 hydrolysis, Appl Catal B Environ 26: 207-215 (2000). |
| [30] | Zeng TY, Qiu Y, Chen LH, Song X, Microstrusture and phase evolution of TiO2 precursors prepared by peptization-hydrolysis method using polycarboxylic acid as peptizing agent, Mater Chem Phys 56: 163-170 (1998). |
| [31] | Zima YM, Karakchiev LG, Lyakhov NZ, Synthesis and physicochemical properties of hydrated titanium dioxide sol, Colloid J 4: 471-475 (1998). |
| [32] | Eremenko BV, Bezuglaya TN, Savitskaya AN, Malysheva ML, Kozlov IS, Bogodist LG, Stability of aqueous dispersions of the hydrated titanium dioxide prepared by titanium tetrachloride hydrolysis, Colloid J 63: 173–178 (2001). |
| [33] | Ravishankar TN, Vaz MO, Teixeira SR, The effects of surfactant in the sol–gel synthesis of CuO/TiO2 nanocomposites on its photocatalytic activities under UV-visible and visible l light illuminations, New J Chem 44: 1888-1904 (2020). |
APA Style
Ming-Hsien Lu, Yu-Wen Chen. (2021). Preparation of TiO2 Sols with High Solid Contents by Sol Gel Method. International Journal of Biochemistry, Biophysics & Molecular Biology, 6(2), 26-33. https://doi.org/10.11648/j.ijbbmb.20210602.11
ACS Style
Ming-Hsien Lu; Yu-Wen Chen. Preparation of TiO2 Sols with High Solid Contents by Sol Gel Method. Int. J. Biochem. Biophys. Mol. Biol. 2021, 6(2), 26-33. doi: 10.11648/j.ijbbmb.20210602.11
AMA Style
Ming-Hsien Lu, Yu-Wen Chen. Preparation of TiO2 Sols with High Solid Contents by Sol Gel Method. Int J Biochem Biophys Mol Biol. 2021;6(2):26-33. doi: 10.11648/j.ijbbmb.20210602.11
Share This Article
Twitter
Linked In
Facebook
Copy
Download@article{10.11648/j.ijbbmb.20210602.11,
author = {Ming-Hsien Lu and Yu-Wen Chen},
title = {Preparation of TiO2 Sols with High Solid Contents by Sol Gel Method},
journal = {International Journal of Biochemistry, Biophysics & Molecular Biology},
volume = {6},
number = {2},
pages = {26-33},
doi = {10.11648/j.ijbbmb.20210602.11},
url = {https://doi.org/10.11648/j.ijbbmb.20210602.11},
eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ijbbmb.20210602.11},
abstract = {Titanium oxide has been extensively used as a photocatalytic material because of its excellent UV light-responsive effect, high refractive index, and high chemical stability. TiO2 in anatase phase for applications in optical or electronic devices and photocatalysis has generally been used in the form of a thin film. The aim of this study was to prepare a stable TiO2 sol with high solid content. Therefore one can use less coating time to have a mono layer of TiO2 film on the substrate. In this study, TiCl4 was slowly added to the distilled water in an ice bath. Aqueous solution of sodium hydroxide was added to adjust the pH of the solution to between 8 and 12 to form titanium hydroxide gel. After aging for a period of time, the Ti(OH)4 gel was filtered and sufficiently washed. The filtered cake was repulped in water. Hydrochloric acid, as a catalyst for polycondensation, was slowly added to the solution with stirring. After poly-condensation reaction and crystallization, a transparent suspended TiO2 sol was formed. XRD results show that the crystalline phase was anatase. The suspended TiO2 particles were rhombus primary particles with the major axis ca. 20 nm and the minor axis ca. 5 nm. The sample prepared at pH 8 had the largest BET surface area of 141 cm3/g among all samples. The best preparation condition to have the smallest TiO2 particles are Ti: H = 1: 1 (atomic ratio), 10% solid content of TiO2, and hydroxypropyl cellulose with viscosity of 150-400 cps as a surfactant. The thin film was obtained by dip-coating the glass in TiO2 sol. Since the sol had high solid content, the coating time became less. The dip-coating on glass was less than three times to have one monolayer TiO2. The transparent TiO2 thin film had super-hydrophilicity after illumination by UV light.},
year = {2021}
}
TY - JOUR T1 - Preparation of TiO2 Sols with High Solid Contents by Sol Gel Method AU - Ming-Hsien Lu AU - Yu-Wen Chen Y1 - 2021/07/22 PY - 2021 N1 - https://doi.org/10.11648/j.ijbbmb.20210602.11 DO - 10.11648/j.ijbbmb.20210602.11 T2 - International Journal of Biochemistry, Biophysics & Molecular Biology JF - International Journal of Biochemistry, Biophysics & Molecular Biology JO - International Journal of Biochemistry, Biophysics & Molecular Biology SP - 26 EP - 33 PB - Science Publishing Group SN - 2575-5862 UR - https://doi.org/10.11648/j.ijbbmb.20210602.11 AB - Titanium oxide has been extensively used as a photocatalytic material because of its excellent UV light-responsive effect, high refractive index, and high chemical stability. TiO2 in anatase phase for applications in optical or electronic devices and photocatalysis has generally been used in the form of a thin film. The aim of this study was to prepare a stable TiO2 sol with high solid content. Therefore one can use less coating time to have a mono layer of TiO2 film on the substrate. In this study, TiCl4 was slowly added to the distilled water in an ice bath. Aqueous solution of sodium hydroxide was added to adjust the pH of the solution to between 8 and 12 to form titanium hydroxide gel. After aging for a period of time, the Ti(OH)4 gel was filtered and sufficiently washed. The filtered cake was repulped in water. Hydrochloric acid, as a catalyst for polycondensation, was slowly added to the solution with stirring. After poly-condensation reaction and crystallization, a transparent suspended TiO2 sol was formed. XRD results show that the crystalline phase was anatase. The suspended TiO2 particles were rhombus primary particles with the major axis ca. 20 nm and the minor axis ca. 5 nm. The sample prepared at pH 8 had the largest BET surface area of 141 cm3/g among all samples. The best preparation condition to have the smallest TiO2 particles are Ti: H = 1: 1 (atomic ratio), 10% solid content of TiO2, and hydroxypropyl cellulose with viscosity of 150-400 cps as a surfactant. The thin film was obtained by dip-coating the glass in TiO2 sol. Since the sol had high solid content, the coating time became less. The dip-coating on glass was less than three times to have one monolayer TiO2. The transparent TiO2 thin film had super-hydrophilicity after illumination by UV light. VL - 6 IS - 2 ER -