Increase in world population has led to more energy demand. Therefore, there is need for utilization of green and renewable energy. Dye sensitized solar cells (DSSCs) based on TiO2 have attracted a lot of attention as an alternative source as compared to current silicon technology. In this study, TiO2 thin films were deposited on doped fluorine tin oxide layer (FTO) glass substrates using sol-gel doctor blading technique. The films were annealed at different rates (1step, 2°C/min and 1°C/min) up to a temperature of 450°C followed by sintering at this temperature for 30 minutes. UV-VIS spectrophotometry was employed to probe the absorbance and reflectance of the films. It was found that, the optical parameters, such as the reflectance, the real (ε1) and imaginary (ε2) parts of dielectric constant, skin depth, Urbach energy and the energy gap; all depend on the annealing rate. The skin depth for the samples in visible region were found to increase from 6.319 x 10-5 to 11.968 x 10-5 cm-1 due to annealing. The Optical band energy (Eg) decreased from 5.04eV for as deposited film to 4.35eV at annealing rate of 1°C/min for direct allowed and from 2.76 to 2.56 eV for indirect transitions. Urbach tails in weak absorption region decreased with annealing rate. Urbach energies (Eu) were in the range of 432-505 meV for as deposited and annealed films. This was used to account for the disorder of the films. An inverse relation between Urbach energy and optical band energy as result of annealing rate was reported.
| Published in | American Journal of Nanosciences (Volume 7, Issue 1) |
| DOI | 10.11648/j.ajn.20210701.15 |
| Page(s) | 28-34 |
| Creative Commons |
This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited. |
| Copyright |
Copyright © The Author(s), 2024. Published by Science Publishing Group |
Annealing Rate, Band Gap, Skin Depth and Urbach Energy
| [1] | Lyson-Sypien, B., Czapla, A., Lubecka, M. (2013) Gas sensing properties of TiO2–SnO2 nanomaterials. Sensor Actuators 187, 445–454. |
| [2] | Li, C. P., Wang, J. F., Su, W. B. (2003) Effect of sinter temperature on the electrical properties of TiO2 based capacitor-varistors. Material Letters 57, 1400–1405. |
| [3] | Michael, G. (2001) Sol–gel processed TiO2 films for photovoltaic applications. Journal of Sol Gel. Science Technology 22, 7–13. |
| [4] | Tachibana, Y., Ohsaki, H., Hayashi, A. (2000). TiO2–X sputter for high rate deposition of TiO2. Vacuum. 59, 836–843. |
| [5] | Ben Naceur J., Gaidi M., Bousbih F., Mechiakh R. and Chtourou R. (2012) "Annealing effects on microstructural and optical properties of Nanostructured-TiO2 thin films prepared by sol–gel technique", Current Applied Physics. |
| [6] | Huang, M., Yu, S., Li, B. (2014). Influence of preparation methods on the structure and catalytic performance of SnO2-doped TiO2 photocatalysts. Ceram International 40, 13305–13312. |
| [7] | Chen Y. F., Lee C. Y., Yeng M. Y. and Chiu H. T. (2003). Preparing titanium oxide with various morphologies. Materials Chemistry and Physics. 81: 39–44. |
| [8] | Palik E. D., (1991). Handbook of Optical Constants of Solids, vol. II, Academic Press, 795. |
| [9] | Naceur J. B., Gaidi M., Bousbih F., Mechiakh R. and Chtourou R. (2012). Annealing effects on microstructural and optical properties of Nanostructured-TiO2 thin films prepared by sole-gel technique. Current Applied Physics 12: 422-428. |
| [10] | Wang X., Wu G., Zhou B. and Shen J. (2013). Optical Constants of Crystallized TiO2 Coatings Prepared by Sol-Gel Process. Materials, 6, 2819-2830. |
| [11] | Vasuki T, Saroja M, Venkatachalam M and Shankar, (2015). Synthesis and characterization of TiO2 thin film for photocatalytic degradation of textile dye effluent. International Journal of Recent Scientific Research. 4, 3511-3514. |
| [12] | Choudhury, B., Borah, B., and Choudhury, A. (2013) Ce-Nd codoping effect on the structural and optical properties of TiO2 nanoparticles, Materials Science and Engineering B, 178 (4), 239-247. |
| [13] | Mo, S. D., and Ching, W. Y. Electronic and optical properties of three phases of titanium dioxide: Rutile, anatase, and brookite, Physics Rev. B 51 (19), 1 3023, 1995. |
| [14] | T. Sekiya, K. Ichimura, M. Igarashi, S. Kurita, Absorption spectra of anatase TiO2 single crystals heat treated under oxygen atmosphere, Journal Physical Chemistry Solids. 61 (8), 1237-1242, 2000. |
| [15] | Liu, G., et al. Enhanced photoactivity of oxygen deficient anatase TiO2 sheets with dominant {101} facets, Journal of Physical Chemistry. 113 (52), 21784–21788, 2009. |
| [16] | Komaguchi, K., et al. Electron transfer reactions of oxygen species on TiO2 nanoparticles induced by sub band gap illumination, Journal Physical Chemistry. 114 (2), 1240–1245, 2010. |
| [17] | Kuznetsov, V. N., & Serpone, N. On the origin of spectral bands in the visible spectral bands in the visible absorption spectra light active TiO2 specimens analysis and assignments, Journal Physical Chemistry. 113 (34), 15110–15123, 2009. |
| [18] | Chiodo L., Lastra J. M., Iacomino A., Ossicini S., Zhao J., Petek H., Rubio A. (2010) Self-energy and excitonic effects in the electronic and optical properties of TiO2 crystalline phases, Physics Review 82 (4), 045207. |
| [19] | Boubaker K. (2011). A physical explanation to the controversial Urbach tailing universality, The European Physics Journal Plus, 126, 10. |
| [20] | Natarajan C., Nogami G., Journal of The Electrochemical Society 143 (1996) 1547-1570. |
| [21] | Karuppuchamy S., Nonomura K., Yoshida T., Sugiura T., Minoura H., Solid State Ionics. 151 (2002) 19-27. |
| [22] | Garapon C., Champeaux C., Mugnier J., Panczer G., Marchet P., Catherinot A. and Jacquier B. (1996). Preparation of TiO2 thin films by pulsed laser deposition for wave guiding applications Appl. Surf. Sci. 96-98 836-841. |
| [23] | Huang H., Yao X., J. Cryst. Growth 268 (2004) 564-567. |
| [24] | Wang F. X., Hwangbo C. K., Jung B. Y., Lee J. H., Park B. H., Kim N. Y., Surf. Coat. Technol. 201 (2007) 5367-5370. |
| [25] | Antunes R. A., Deoliveira M. C. L., Pillis M. F., Int. J. Electrochem. Sci. 8 (2013) 1487–1500. |
| [26] | Benjamin M. J., Simon W. M., and James M. N. (2018) “Effect of Annealing Rates on Surface Roughness of TiO2 Thin films.” Journal of Materials Physics and Chemistry, 6 (2): 43-46. |
| [27] | Sta I, Jlassi M, Hajji M, Boujmil M. F, and Jerbi R. (2014). Structural and optical properties of TiO2 thin films prepared by spin coating. Journal of Sol-Gel Science and Technology 72: 421-427. |
| [28] | Theiss, W. (2000). Scout thin films analysis software handbook, edited by Theiss M (Hand and Software Aachen German) www.mtheiss.com. |
| [29] | Sharma N, Prabakar K, Ilango S, Dash S and Tyagi A K (2015). Application of dynamic scaling theory for growth kinetic studies of AlN-thin films deposited by ion beam sputtering in reactive assistance of nitrogen plasma, Applied Surface Science 347: 875-9. |
| [30] | Sharma N, Ilango S, and Dash S and Tyagi A K 2015 XPS studies on AlN thin films grown by ion beam sputtering in reactive assistance of N+ /N2+ ions: Substrate temperature induced compositional variations arXiv: 1510.00541. |
| [31] | Boubaker K 2011 A physical explanation to the controversial Urbach tailing universality The European Physical Journal Plus 126 1-4. |
| [32] | Urbach, F., The Long-Wavelength Edge of Photographic Sensitivity and of the Electronic Absorption of Solids, Phys. Rev., 92, 1324-1325 (1953). |
| [33] | Tauc, J., Amorphous and Liquid Semiconductors, Plenum Press, New York, (1974). |
| [34] | Tauc, J., R. Grigorovici and Vancu, A. Optical Properties and Electronic Structure of Amorphous Germanium, Phys. Status Solidi, 15, 627-637 (1966). |
| [35] | M. Balkanski, R. F. Wollis; “Semiconductor physics and application”, Óxford University Press (2000). |
| [36] | C. Fournier, O. Bamiduro, H. Mustafa, R. Mundle, R. B. Konda, F. Williams and A. K. Pradhan, Semiconductor Science and Technology., 2008, 23, 085019. |
| [37] | Y. Kim and J. Y. Leem, Phys. B, 2015, 476, 71–76. |
| [38] | Akl, A. A. Kamal H., Abdel-Hady K. (2006) "Fabrication and characterization of sputtered titanium dioxide films", Applied Surface Science, 252: 8651–8656. |
| [39] | Cheng, W. X., Ding, A. L., Qiu, P. S., He, X. Y. and Zheng, X. S. H. (2003). Optical and dielectric properties of highly oriented (Zr0.8, Sn0.2) TiO4 thin films prepared by rf magnetron sputtering, Applied Surface Science 214: 136-142. |
| [40] | Tauc, J. in: J. Tauc (Ed.), Amorphous and Liquid Semiconductors, Plenum Press, London and New York, 1974. |
| [41] | El-Nahass, M. M., Soliman, H. S., El-Denglawey, A. (2016). Absorption edge shift, opticalconductivity, and energy loss function of nano thermal-evaporated N-typeanatase TiO2 films. Appl Phys A; 122: 775. |
| [42] | Mathews, N. R., Morales, E. R., Cortés-Jacome, M. A., & Antonio, J. T. (2009). TiO2 thin films–Influence of annealing temperature on structural, optical and photocatalytic properties. Solar Energy, 83 (9), 1499-1508. |
| [43] | Wibowo, K. M., Sahdan, M. Z., Asmah, M. T., Saim, H., Adriyanto, F., & Hadi, S. (2017), August). Influence of Annealing Temperature on Surface Morphological and Electrical Properties of Aluminum Thin Film on Glass Substrate by Vacuum Thermal Evaporator. In IOP Conference Series: Materials Science and Engineering (Vol. 226, No. 1, p. 012180). IOP Publishing. |
| [44] | Sharma N., Sharma S., Prabakar K., Amirthapandian S., Ilango S., Dash S. and Tyagi A. K. Optical band gap and associated band-tails in nanocrystalline AlN thin films grown by reactive IBSD at different substrate temperatures Material Science Group, Indira Gandhi Centre for Atomic Research 603102. |
| [45] | Al-Shomara, S. M., Alahmad W. R. (2019), Annealing temperature effect on structural, optical and photocatalytic activity of nanocrystalline TiO2 films prepared by sol-gel method used for solar cell application, Digest Journal of Nanomaterials and Biostructures, 14, 617-625. |
| [46] | Hasan M. M., Haseeb A. S. M. A., Saidur R., and Masjuki H. H. (2009). Effects of Annealing Treatment on Optical Properties of Anatase TiO2 Thin Films. Journal of Nuclear Science and Technology. |
| [47] | Sankar S. and Gopchandran, K. G (2009). Effect of annealing on the structural, electrical and optical properties of nanostructured TiO2 thin films. Crystal Research and Technology. 44: 989-994. |
| [48] | Pawar, S. Chougule, M. Godse, P. Jundale, D. Pawar S. Raut, B. and Patil, V. (2011). Effect of annealing on structure, morphology, electrical and optical properties of nanocrystalline TiO2 thin films. Journal of Nano- Electron Physics. 3: 185–192. |
| [49] | Khan F. U., Zubair M., Ansar M. Z., Alamgir M. K., Nadeem S. (2016) "Effect of Annealing Temperature on the Structural and Optical Properties of TiO2 Thin Film Prepared by Sol-gel Method", Journal of Scientific Research, 8 (3), 267-272. |
| [50] | Mathews, N. R. Morales, E. R. Corte´s-Jacome, M. A., and Toledo Antonio J. A., (2009) TiO2 thin films – Influence of annealing temperature on structural, optical and photocatalytic properties, Solar Energy 83: 1499–1508. |
| [51] | Atefeh T. and Davood R. (2016). The annealing temperature dependence of anatase TiO2 thin films prepared by the electron-beam evaporation method, Semiconductor Science and Technology. 31: 12. |
| [52] | El Fanaoui1, A. Taleb, A. El Hamri, E. Boulkaddat, L. Kirou, H. Atourki, L. Ihlal A. and Bouabid K. (2016) Effect of heat treatment on TiO2 thin films properties, Journal of Material Environmental Science, 7 (3) 907-914. |
APA Style
Geoffrey Gitonga Riungu, Simon Waweru Mugo, James Mbiyu Ngaruiya, Gitonga Mbae John, Nelson Mugambi. (2021). Optical Band Energy, Urbach Energy and Associated Band Tails of Nano Crystalline TiO2 Films at Different Annealing Rates. American Journal of Nanosciences, 7(1), 28-34. https://doi.org/10.11648/j.ajn.20210701.15
ACS Style
Geoffrey Gitonga Riungu; Simon Waweru Mugo; James Mbiyu Ngaruiya; Gitonga Mbae John; Nelson Mugambi. Optical Band Energy, Urbach Energy and Associated Band Tails of Nano Crystalline TiO2 Films at Different Annealing Rates. Am. J. Nanosci. 2021, 7(1), 28-34. doi: 10.11648/j.ajn.20210701.15
AMA Style
Geoffrey Gitonga Riungu, Simon Waweru Mugo, James Mbiyu Ngaruiya, Gitonga Mbae John, Nelson Mugambi. Optical Band Energy, Urbach Energy and Associated Band Tails of Nano Crystalline TiO2 Films at Different Annealing Rates. Am J Nanosci. 2021;7(1):28-34. doi: 10.11648/j.ajn.20210701.15
Share This Article
Twitter
Linked In
Facebook
Copy
Download@article{10.11648/j.ajn.20210701.15,
author = {Geoffrey Gitonga Riungu and Simon Waweru Mugo and James Mbiyu Ngaruiya and Gitonga Mbae John and Nelson Mugambi},
title = {Optical Band Energy, Urbach Energy and Associated Band Tails of Nano Crystalline TiO2 Films at Different Annealing Rates},
journal = {American Journal of Nanosciences},
volume = {7},
number = {1},
pages = {28-34},
doi = {10.11648/j.ajn.20210701.15},
url = {https://doi.org/10.11648/j.ajn.20210701.15},
eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ajn.20210701.15},
abstract = {Increase in world population has led to more energy demand. Therefore, there is need for utilization of green and renewable energy. Dye sensitized solar cells (DSSCs) based on TiO2 have attracted a lot of attention as an alternative source as compared to current silicon technology. In this study, TiO2 thin films were deposited on doped fluorine tin oxide layer (FTO) glass substrates using sol-gel doctor blading technique. The films were annealed at different rates (1step, 2°C/min and 1°C/min) up to a temperature of 450°C followed by sintering at this temperature for 30 minutes. UV-VIS spectrophotometry was employed to probe the absorbance and reflectance of the films. It was found that, the optical parameters, such as the reflectance, the real (ε1) and imaginary (ε2) parts of dielectric constant, skin depth, Urbach energy and the energy gap; all depend on the annealing rate. The skin depth for the samples in visible region were found to increase from 6.319 x 10-5 to 11.968 x 10-5 cm-1 due to annealing. The Optical band energy (Eg) decreased from 5.04eV for as deposited film to 4.35eV at annealing rate of 1°C/min for direct allowed and from 2.76 to 2.56 eV for indirect transitions. Urbach tails in weak absorption region decreased with annealing rate. Urbach energies (Eu) were in the range of 432-505 meV for as deposited and annealed films. This was used to account for the disorder of the films. An inverse relation between Urbach energy and optical band energy as result of annealing rate was reported.},
year = {2021}
}
TY - JOUR T1 - Optical Band Energy, Urbach Energy and Associated Band Tails of Nano Crystalline TiO2 Films at Different Annealing Rates AU - Geoffrey Gitonga Riungu AU - Simon Waweru Mugo AU - James Mbiyu Ngaruiya AU - Gitonga Mbae John AU - Nelson Mugambi Y1 - 2021/03/09 PY - 2021 N1 - https://doi.org/10.11648/j.ajn.20210701.15 DO - 10.11648/j.ajn.20210701.15 T2 - American Journal of Nanosciences JF - American Journal of Nanosciences JO - American Journal of Nanosciences SP - 28 EP - 34 PB - Science Publishing Group SN - 2575-4858 UR - https://doi.org/10.11648/j.ajn.20210701.15 AB - Increase in world population has led to more energy demand. Therefore, there is need for utilization of green and renewable energy. Dye sensitized solar cells (DSSCs) based on TiO2 have attracted a lot of attention as an alternative source as compared to current silicon technology. In this study, TiO2 thin films were deposited on doped fluorine tin oxide layer (FTO) glass substrates using sol-gel doctor blading technique. The films were annealed at different rates (1step, 2°C/min and 1°C/min) up to a temperature of 450°C followed by sintering at this temperature for 30 minutes. UV-VIS spectrophotometry was employed to probe the absorbance and reflectance of the films. It was found that, the optical parameters, such as the reflectance, the real (ε1) and imaginary (ε2) parts of dielectric constant, skin depth, Urbach energy and the energy gap; all depend on the annealing rate. The skin depth for the samples in visible region were found to increase from 6.319 x 10-5 to 11.968 x 10-5 cm-1 due to annealing. The Optical band energy (Eg) decreased from 5.04eV for as deposited film to 4.35eV at annealing rate of 1°C/min for direct allowed and from 2.76 to 2.56 eV for indirect transitions. Urbach tails in weak absorption region decreased with annealing rate. Urbach energies (Eu) were in the range of 432-505 meV for as deposited and annealed films. This was used to account for the disorder of the films. An inverse relation between Urbach energy and optical band energy as result of annealing rate was reported. VL - 7 IS - 1 ER -
Information
Email: